LG Chemical SEETEC BF415 LDPE
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | LG Chemical |
| Trade Name | SEETEC |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical SEETEC BF415 LDPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics: Good Processability and Excellent Optical Properties Applications: Masking filmCAS No. 9002-88-4Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.922 - 0.926 g/cc | 0.922 - 0.926 g/cc | ASTM D1505 |
| Melt Flow | 1.6 - 2.0 g/10 min @Load 2.61 kg, Temperature 190 °C |
1.6 - 2.0 g/10 min @Load 5.75 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 12.3 MPa | 1780 psi | 500mm/min; ASTM D638 |
| Film Elongation at Break, MD | 300 % | 300 % | 500 mm/min; ASTM D638 |
| Film Elongation at Break, TD | 550 % | 550 % | 500 mm/min; ASTM D638 |
| Elongation at Break | 550 % | 550 % | 500 mm/min; ASTM D638 |
| 2% Secant Modulus | 1.20 GPa | 174 ksi | 500mm/min; ASTM D638 |
| Elmendorf Tear Strength MD | 400 g | 400 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 180 g | 180 g | ASTM D1922 |
| Dart Drop Test | 55.0 g | 0.121 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 25.5 MPa | 3700 psi | 500mm/min, Ultimate; ASTM D638 |
| Film Tensile Strength at Break, TD | 23.5 MPa | 3410 psi | 500mm/min, Ultimate; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 112 °C | 234 °F | 10°C/min; ASTM D3418 |
| Vicat Softening Point | 92.0 °C | 198 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 5.0 % | 5.0 % | ASTM D1003 |
| Gloss | 95 % | 95 % | 45°; ASTM D2457 |
Users viewing this material also viewed the following:
- Petromont 8001 High Density Polyethylene Resin
- LG Chemical BM662B ABS, Heat Resistance
- Lotte Chemical Titan TITANLENE® LDF200YZ Low density polyethylene
- Techmer ES HiFill FR® PBT FR X
- Samsung Cheil Industries Starex® TX-0520 TRABS, Unreinforced
- Eagle Brass 521 Phosphor Bronzes 8% C, Spring
- Diamond Polymers NPP 808 C3 TDS Polycarbonate Alloy
- Arkema Group Orgalloy® LT 5050 Flexible Nylon Alloy (Conditioned)
- Gouda Vuurvast FI 25-12 Insulating Refractory Brick
Copyright © lookpolymers.com All Rights Reserved