Nilit FRIANYL B63 HS-GV25 Nylon 6 for injection molding, 25% glass fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 HS-GV25 Nylon 6 for injection molding, 25% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| Water Absorption | 2.0 - 3.0 % | 2.0 - 3.0 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 7.0 % | 6.0 - 7.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.011 - 0.019 cm/cm | 0.011 - 0.019 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 106 MPa | 15400 psi | ISO 2039-1 |
| Tensile Strength at Break | 114 MPa | 16500 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 6.05 GPa | 877 ksi | ISO 527 |
| Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
| Flexural Modulus | 5.10 GPa | 740 ksi | ISO 178 |
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | DIN 53453 |
| NB | NB | ISO 179/1eU | |
| 5.30 J/cm² @Temperature -40.0 °C |
25.2 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.80 J/cm² | 8.57 ft-lb/in² | DIN 53453 |
| 1.90 J/cm² | 9.04 ft-lb/in² | ISO 179/1eA | |
| 1.20 J/cm² @Temperature -40.0 °C |
5.71 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 100 °C | 212 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Nye Lubricants 362F (RL) Synthetic Oil
- MetalTek MTEK 230 Cast UNS C95500 Aluminum Bronze
- Seals Eastern 7336 Highly Saturated Nitrile Rubber
- Borealis Borclean™ HC320BF Polypropylene Homopolymer for Capacitor Film
- Von Roll Isola IMI E-Solder® 3021 Electrically Conductive Adhesive
- A. Schulman FORMION™ FI 225 30% Glass Fiber Reinforced Ionomer / Nylon Alloy
- Dow SE SLR-4610 H Solution polymerized Styrene Butadiene Rubber (S-SBR)
- Fainplast Compounds GSO 65/33 Flexible PVC, Injection Molding for Footwear
Copyright © lookpolymers.com All Rights Reserved