Nilit FRIANYL B63 CU90 Nylon 6.6 for injection molding, 90% copper filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 CU90 Nylon 6.6 for injection molding, 90% copper filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 5.12 g/cc | 0.185 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 - 0.60 % | 0.30 - 0.60 % | ISO 62 |
| Water Absorption at Saturation | 2.0 - 3.0 % | 2.0 - 3.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0020 - 0.0070 cm/cm | 0.0020 - 0.0070 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 125 MPa | 18100 psi | ISO 2039-1 |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | ISO 527 |
| Elongation at Break | 16 % | 16 % | ISO 527 |
| Tensile Modulus | 1.40 GPa | 203 ksi | ISO 527 |
| Flexural Strength | 34.0 MPa | 4930 psi | ISO 178 |
| Flexural Modulus | 4.30 GPa | 624 ksi | ISO 178 |
| Charpy Impact Unnotched | 1.90 J/cm² | 9.04 ft-lb/in² | DIN 53453 |
| 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179/1eU | |
| 0.800 J/cm² @Temperature -40.0 °C |
3.81 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/1eA |
| 0.500 J/cm² | 2.38 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 180 °C | 356 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+9 ohm-cm | 1.00e+9 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
Users viewing this material also viewed the following:
- Reliance Industries Relene F56003 Polyethylene
- Lanxess Durethan® BKV 230 H2.0 901510 Copolyamide, 30% Glass Fiber
- Momentive Performance Materials RTV8112 White General Purpose Potting/Encapsulating Compound
- Solvay TECHNYL® A 218 V40 Black 21 NHFE PA66, 40% glass fiber, Conditioned
- Sibur 1045-12 Compound 948 Polyvinyl Chloride (PVC)
- Teknor Apex Telcar® TL-1934A BLK 111 Thermoplastic Elastomer
- Hexcel® HexForce™ 8800 Fiber Glass Fabric
- Dow Corning SYL-OFF® PMCPEM 7974 Emulsion Coating
- Aremco Corr-Paint™ CP4010-S1 High Temperature Protective Coating, Silicone
- Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Aged 732°C (1350°F)/8hr/AC
Copyright © lookpolymers.com All Rights Reserved