Lanxess Pocan® B 1700 000000 PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Extrusion Grade , Polybutylene Terephthalate (PBT), Unreinforced, Molded
Manufacturer Lanxess
Trade Name Pocan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Pocan® B 1700 000000 PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT, non-reinforced, extrusion, food contact
Physical Properties Metric English Comments
Density 1.30 g/cc
0.0470 lb/in³
ISO 1183
Water Absorption 0.50 %
0.50 %
Test Sim. to ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C/50% R.H.; Test Sim. to ISO 62
Viscosity Test 158 cm³/g
158 cm³/g
Viscosity number; ISO 307, 1157, 1628
Melt Flow 14 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 14 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 Estimated using room temperature density; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 55.0 MPa
7980 psi
ISO 527-1/-2
Elongation at Break >= 50 %
>= 50 %
Nominal; ISO 527-1/-2
Elongation at Yield 4.0 %
4.0 %
ISO 527-1/-2
Tensile Modulus 2.60 GPa
377 ksi
ISO 527-1/-2
Charpy Impact Unnotched 23.0 J/cm²

@Temperature -30.0 °C
 109 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
<= 1.00 J/cm²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Impact 3877
3877
Puncture maximum force (N); ISO 6603-2
3926

@Temperature -30.0 °C
 3926

@Temperature -22.0 °F
 Puncture maximum force (N); ISO 6603-2
Puncture Energy 23.0 J
17.0 ft-lb
ISO 6603-2
16.0 J

@Temperature -30.0 °C
 11.8 ft-lb

@Temperature -22.0 °F
 ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 130 µm/m-°C
72.2 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 130 µm/m-°C
72.2 µin/in-°F
ISO 11359-1/-2
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 45.0 °C
113 °F
ISO 75-1/-2
Flammability, UL94 HB
HB
IEC 60695-11-10
HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
 IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance <= 1.00e+15 ohm
<= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
 3.2

@Frequency 1.00e+6 Hz
 IEC 60250
3.4

@Frequency 100 Hz
 3.4

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 30.0 kV/mm
762 kV/in
IEC 60243-1
Dissipation Factor 0.0015

@Frequency 100 Hz
 0.0015

@Frequency 100 Hz
 IEC 60250
0.020

@Frequency 1.00e+6 Hz
 0.020

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Injection Molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection Molding; ISO 10724
Descriptive Properties Value Comments
Form Pellets
ISO Shortname ISO 7792-1-PBT,G,13-030
Processing Other extrusion