Nilit FRIANYL A63 SG15 Nylon 6.6 for injection molding, 15% mineral filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Mineral Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 SG15 Nylon 6.6 for injection molding, 15% mineral filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.0 % | 1.5 - 2.0 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 8.0 % | 6.0 - 8.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.017 - 0.025 cm/cm | 0.017 - 0.025 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 142 MPa | 20600 psi | ISO 2039-1 |
| Tensile Strength at Break | 88.0 MPa | 12800 psi | ISO 527 |
| Elongation at Break | 8.0 % | 8.0 % | ISO 527 |
| Tensile Modulus | 4.50 GPa | 653 ksi | ISO 527 |
| Flexural Strength | 93.0 MPa | 13500 psi | ISO 178 |
| Flexural Modulus | 3.50 GPa | 508 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 0.530 J/cm² | 2.52 ft-lb/in² | ISO 179/1eA |
| 0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable WR7426L Polyvinyl Chloride, Flexible (PVC, Flexible)
- SABIC Innovative Plastics LNP LUBRICOMP ML004 PP
- SABIC Innovative Plastics LNP LUBRICOMP RFG16 PA 66 (Europe-Africa-Middle East)
- American Elements Bismuth Oxide Nanopowder
- Aremco Pyro-Paint™ 634-AL High Temperature Refractory Coating
- Arlon 44570R025 0.025" (0.635 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Solvay Specialty Polymers Torlon® 7130 Polyamide-imide (PAI) (Unverified Data**)
- Indium Corp. Indalloy 195 Gold Solder Alloy
- DuPont Performance Polymers Zytel® 70G33HS1L NC010 Nylon 66 (Unverified Data**)
- Overview of materials for Polysulfone, 20% Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved