- Nilit FRIANYL A63 GV50 Nylon 6.6 for injection molding, 50% glass fiber reinforced
Nilit FRIANYL A63 GV50 Nylon 6.6 for injection molding, 50% glass fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 GV50 Nylon 6.6 for injection molding, 50% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 |
| Water Absorption | 0.70 - 1.7 % | 0.70 - 1.7 % | ISO 62 |
| Water Absorption at Saturation | 0.20 - 1.0 % | 0.20 - 1.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0020 - 0.010 cm/cm | 0.0020 - 0.010 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 200 MPa | 29000 psi | ISO 2039-1 |
| Tensile Strength at Break | 230 MPa | 33400 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 16.0 GPa | 2320 ksi | ISO 527 |
| Flexural Strength | 290 MPa | 42100 psi | ISO 178 |
| Flexural Modulus | 14.7 GPa | 2130 ksi | ISO 178 |
| Charpy Impact Unnotched | 5.40 J/cm² | 25.7 ft-lb/in² | DIN 53453 |
| NB | NB | ISO 179/1eU | |
| 5.00 J/cm² @Temperature -40.0 °C |
23.8 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | DIN 53453 |
| 1.40 J/cm² | 6.66 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 130 °C | 266 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXD103 PC (Europe-Africa-Middle East)
- Solvay Engineered Polymers SEQUEL® 1783 Engineered Polyolefin (discontinued **)
- ITW Plexus Plexusâ„¢ MA555 Methacrylate Adhesive
- Techmer ES Electrafil® J-3/CF/10 Nylon 6, 10% Carbon Fiber Reinforced
- Solvay Specialty Polymers Polymist® XPP 535 Polytetrafluoroethylene (PTFE)
- Techmer ES Elastoblend® PA6/6 GF8 IM3 BK 8% Glass Filled
- China-Yixing Longly Refractories Plate Corundum-Mullite
- AK Steel Aluminized Carbon Steel, Deep Drawing Steel (DDS Type B), Standard Grade
- Gromax CCP PBT 5630-200C 30% Glass Fiber Filled
Copyright © lookpolymers.com All Rights Reserved