Network Polymers Kepital® F40-03
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | Network Polymers |
| Trade Name | Kepital® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers Kepital® F40-03.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Natural Acetal CopolymerInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.22 % | 0.22 % | 23°C at 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.020 cm/cm | 0.020 in/in | ASTM D955 |
| Melt Flow | 52 g/10 min @Load 2.16 kg, Temperature 190 °C |
52 g/10 min @Load 4.76 lb, Temperature 374 °F |
Procedure A Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 80 | 80 | ASTM D785 |
| Tensile Strength at Break | 61.4 MPa | 8900 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Flexural Strength | 91.7 MPa | 13300 psi | ASTM D790 |
| Flexural Modulus | 2.65 GPa | 384 ksi | ASTM D790 |
| Poissons Ratio | 0.35 | 0.35 | |
| Shear Strength | 55.2 MPa | 8000 psi | ASTM D732 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 |
| Coefficient of Friction | 0.13 | 0.13 | Against Steel; Westover or Radial Type |
| 0.15 | 0.15 | Against Aluminum; Westover or Radial Type | |
| 0.15 | 0.15 | Against Brass; Westover or Radial Type | |
| 0.20 | 0.20 | Against Kepital; Westover or Radial Type |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 130 µm/m-°C @Temperature 20.0 °C |
72.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Melting Point | 165 °C | 329 °F | 10°C/min heating; DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Vicat Softening Point | 162 °C | 324 °F | 0.125 inch bar, 1 Kg; ASTM D1525 |
| Flammability, UL94 | HB | HB | 0.00311 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 3.7 @Frequency 100 Hz |
3.7 @Frequency 100 Hz |
ASTM D150 |
| 3.7 @Frequency 1e+7 Hz |
3.7 @Frequency 1e+7 Hz |
ASTM D150 | |
| Dissipation Factor | 0.0010 @Frequency 100 Hz |
0.0010 @Frequency 100 Hz |
ASTM D150 |
| 0.0070 @Frequency 1e+6 Hz |
0.0070 @Frequency 1e+6 Hz |
ASTM D150 | |
| Arc Resistance | >= 200 sec | >= 200 sec | ASTM D495 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL1443T PC Copolymer (Europe-Africa-Middle East)
- Lubrizol Advanced Materials PEARLTHANE® 16N80 Thermoplastic Polyurethane Elastomer (discontinued **)
- Global PC/ABS-1216 General Purpose Polycarbonate/ABS Alloy
- SABIC Innovative Plastics LNP LUBRICOMP NL001 PC+ABS
- Solvay Specialty Polymers Tecnoflon® FOR 5351/U Fluoroelastomer
- Tipco Tipcolene® DR 8201 - 20% Talc/Mineral Reinforced, Impact Modified, Polypropylene Copolymer
- ATI Allegheny Ludlum Grade 17 Titanium (UNS R52252)
- Atom Adhesives AA-BOND F112 Epoxy Adhesive
- Abatron AboCast 50-11/AboCure 50-1 Epoxy
- ACC QM 262 QSI Quantum Silicones 60 Durometer Addition Cure Moldmaking Material
Copyright © lookpolymers.com All Rights Reserved