NYCOA 436 PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | NYCOA, Inc. |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NYCOA 436 PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
NSF rated general purpose molding gradeInformation provided by NYCOA, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Water Absorption | 1.7 % | 1.7 % | ASTM D570 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | ASTM D638 |
| Elongation at Break | >= 50 % | >= 50 % | ASTM D638 |
| Flexural Yield Strength | 98.0 MPa | 14200 psi | ASTM D790 |
| Flexural Modulus | 2.552 GPa | 370.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 0.700 mm |
V-2 @Thickness 0.0276 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 °C | 482 °F | |
| Rear Barrel Temperature | 225 °C | 437 °F | |
| Middle Barrel Temperature | 230 °C | 446 °F | |
| Front Barrel Temperature | 250 °C | 482 °F | |
| Nozzle Temperature | 250 °C | 482 °F | |
| Mold Temperature | 80.0 °C | 176 °F | |
| Drying Temperature | 76.0 °C | 169 °F |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PP CIP1001F Polypropylene
- DuPont Elvax® 462 Ethylene-Vinyl Acetate Copolymer Resin (discontinued **)
- Lehmann & Voss LUVOCOM® 19-7669 Polyamide 46, with glass fiber and PTFE
- Freudenberg Simrit E425 Hydrocarbon Elastomer
- Saint-Gobain CHR® 2300-10R UHMW Film Backing Natural Rubber Adhesive Pressure Sensitive Tape
- A. Schulman POLYBATCH™ Hot Pink 50377 Concentrate Based In Polyethylene
- A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT
- Aclo Accutech Polypropylene Homopolymer HP0334G40CL Glass Reinforced Coupled
- Wanhua Chemical Wanthane® WHT-1690AB Polyester Based TPU
Copyright © lookpolymers.com All Rights Reserved