NOVA Chemicals Surpass® FPs021-F Octene sLLDPE Film Resin, 75 Micron Film

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Octene, Film
Manufacturer NOVA Chemicals
Trade Name Surpass®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Surpass® FPs021-F Octene sLLDPE Film Resin, 75 Micron Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FPs021-F complies with the U.S. FDA regulations for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food.NOVA Chemicals' polyethylene resins are biologically and chemically inert.Features: Good stiffness, Easy processability, Very good toughness and strength, Excellent seal properties, Low gelAdditives: Process stabilizer, Antiblock at 3400 ppm, Polymer process aidApplications: Heavy duty shipping sacks requiring very good toughness and high stiffness, Industrial packaging, Industrial liners, Lamination filmFilm properties are typical of blown film extruded on a 2.5" extruder with 4" die and 35-mil die gap at a blow up ratio of 2.5:1, but are dependent upon operating conditions.
Physical Properties Metric English Comments
Density 0.921 g/cc
0.0333 lb/in³
ASTM D 792
Thickness 75.0 microns
2.95 mil
As tested for properties on this data sheet
Melt Flow 0.80 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.80 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 10.0 MPa
1450 psi
ASTM D 882
Film Tensile Strength at Yield, TD 11.0 MPa
1600 psi
ASTM D 882
Film Elongation at Break, MD 760 %
760 %
ASTM D 882
Film Elongation at Break, TD 705 %
705 %
ASTM D 882
Elmendorf Tear Strength MD 1206 g
1206 g
ASTM D 1922
Elmendorf Tear Strength TD 1350 g
1350 g
ASTM D 1922
Elmendorf Tear Strength, MD 16.1 g/micron
409 g/mil
ASTM D 1922
Elmendorf Tear Strength, TD 18.0 g/micron
457 g/mil
ASTM D 1922
Dart Drop 12.1 g/micron
307 g/mil
ASTM D 1709/A
Dart Drop Test 909 g
2.00 lb
F50; ASTM D 1709/A
Film Tensile Strength at Break, MD 50.0 MPa
7250 psi
ASTM D 882
Film Tensile Strength at Break, TD 46.0 MPa
6670 psi
ASTM D 882
1% Secant Modulus, MD 182 MPa
26400 psi
ASTM D 882
1% Secant Modulus, TD 201 MPa
29200 psi
ASTM D 882
Optical Properties Metric English Comments
Haze 22 %
22 %
ASTM D 1003
Gloss 44 %
44 %
At 45°; ASTM D 2457
Processing Properties Metric English Comments
Melt Temperature 200 - 230 °C
392 - 446 °F
Recommended
Descriptive Properties Value Comments
Low Friction Puncture 44 (J/mm)
NOVA Chemicals test method