NOVA Chemicals Sclair® FP026-F Octene LLDPE Film Resin

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer	NOVA Chemicals
Trade Name	Sclair®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	NOVA Chemicals Sclair® FP026-F Octene LLDPE Film Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features: Moderate toughness and strengthGood stiffnessEasy processabilityExcellent seal properties Applications: Heavy duty shipping sacks requiring moderate toughness and high stiffnessIndustrial packagingIndustrial liners Construction films Automatic packaging filmInformation provided by Nova Chemicals

Physical Properties	Metric	English	Comments
Density	0.926 g/cc	0.0335 lb/in³	ASTM D792
Thickness	25.4 microns	1.00 mil
	76.2 microns	3.00 mil
Melt Flow	0.80 g/10 min @Load 2.16 kg, Temperature 190 °C	0.80 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	11.2 MPa	1620 psi	MD, 1 mil; ASTM D882
	12.2 MPa	1770 psi	TD, 1 mil; ASTM D882
	12.2 MPa	1770 psi	TD, 3 mil; ASTM D882
	12.3 MPa	1780 psi	MD, 3 mil; ASTM D882
Elongation at Break	490 %	490 %	MD, 1 mil; ASTM D638
	630 %	630 %	MD, 3 mil; ASTM D882
	680 %	680 %	TD, 3 mil; ASTM D882
	710 %	710 %	TD, 1 mil; ASTM D882
Puncture Energy	0.635 J	0.468 ft-lb	Low Friction Puncture
Elmendorf Tear Strength MD	295 g	295 g	1 mil; ASTM D1922
	1080 g	1080 g	3 mil; ASTM D1922
Elmendorf Tear Strength TD	752 g	752 g	1 mil; ASTM D1922
	1467 g	1467 g	3 mil; ASTM D1922
Dart Drop Test	156 g	0.344 lb	1 mil; ASTM D1709/A
	453 g	0.999 lb	3 mil; ASTM D1709/A
Film Tensile Strength at Break, MD	41.2 MPa	5970 psi	3 mil; ASTM D882
	42.5 MPa	6160 psi	1 mil; ASTM D882
Film Tensile Strength at Break, TD	33.1 MPa	4800 psi	1 mil; ASTM D882
	35.2 MPa	5100 psi	3 mil; ASTM D882
1% Secant Modulus, MD	230.0 MPa	33360 psi	3 mil; ASTM D882
	234.0 MPa	33940 psi	1 mil; ASTM D882
1% Secant Modulus, TD	251 MPa	36400 psi	1 mil; ASTM D882
	260 MPa	37700 psi	3 mil; ASTM D882

Optical Properties	Metric	English	Comments
Haze	13.9 %	13.9 %	1 mil; ASTM D1003
	16.6 %	16.6 %	3 mil; ASTM D1003
Gloss	50 %	50 %	1 mil, at 45°; ASTM D2457
	61 %	61 %	3 mil, at 45°; ASTM D2457

Processing Properties	Metric	English	Comments
Melt Temperature	210 - 230 °C	410 - 446 °F