Hexcel® HexPly® F652 Bismaleimide Resin, Carbon Tape Form

Category Polymer , Thermoset , Polyimide, TS
Manufacturer Hexcel
Trade Name HexPly®
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Hexcel® HexPly® F652 Bismaleimide Resin, Carbon Tape Form.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Material Description: T6T145; Fiber: T300-6KInformation provided by HexCel
Physical Properties Metric English Comments
Density 1.50 - 1.53 g/cc
0.0542 - 0.0553 lb/in³
Laminate
Volatiles <= 2.0 %
<= 2.0 %
Prepreg
Mechanical Properties Metric English Comments
Tensile Strength, Yield 143.6 MPa
<br>@Temperature 177 °C
 20830 psi
<br>@Temperature 351 °F
 Autoclave Cured; [+/- 45°]2s
193.7 MPa
<br>@Temperature 23.0 °C
 28090 psi
<br>@Temperature 73.4 °F
 Autoclave Cured; [+/- 45°]2s
Tensile Modulus 16.7 GPa
<br>@Temperature 177 °C
 2420 ksi
<br>@Temperature 351 °F
 Autoclave Cured; [+/- 45°]2s
18.8 GPa
<br>@Temperature 23.0 °C
 2730 ksi
<br>@Temperature 73.4 °F
 Autoclave Cured; [+/- 45°]2s
Flexural Yield Strength 12.0 MPa
<br>@Temperature 232 °C
 1740 psi
<br>@Temperature 450 °F
 Autoclave Cured; [90°]16; Wet condition
23.0 MPa
<br>@Temperature 177 °C
 3340 psi
<br>@Temperature 351 °F
 Autoclave Cured; [90°]16; Wet condition
28.0 MPa
<br>@Temperature 316 °C
 4060 psi
<br>@Temperature 601 °F
 Autoclave Cured; [90°]16
60.0 MPa
<br>@Temperature 232 °C
 8700 psi
<br>@Temperature 450 °F
 Autoclave Cured; [90°]16
69.6 MPa
<br>@Temperature 177 °C
 10100 psi
<br>@Temperature 351 °F
 Autoclave Cured; [90°]16
105 MPa
<br>@Temperature 23.0 °C
 15200 psi
<br>@Temperature 73.4 °F
 Autoclave Cured; [90°]16
544 MPa
<br>@Temperature 316 °C
 78900 psi
<br>@Temperature 601 °F
 Autoclave Cured; [0°]16
692.9 MPa
<br>@Temperature 232 °C
 100500 psi
<br>@Temperature 450 °F
 Autoclave Cured; [0°]16; Wet condition
1066 MPa
<br>@Temperature 177 °C
 154600 psi
<br>@Temperature 351 °F
 Autoclave Cured; [0°]16; Wet condition
1236 MPa
<br>@Temperature 232 °C
 179300 psi
<br>@Temperature 450 °F
 Autoclave Cured; [0°]16
1434 MPa
<br>@Temperature 177 °C
 208000 psi
<br>@Temperature 351 °F
 Autoclave Cured; [0°]16
1705 MPa
<br>@Temperature 23.0 °C
 247300 psi
<br>@Temperature 73.4 °F
 Autoclave Cured; [0°]16
Flexural Modulus 3.20 GPa
<br>@Temperature 232 °C
 464 ksi
<br>@Temperature 450 °F
 Autoclave Cured; [90°]16; Wet condition
3.40 GPa
<br>@Temperature 316 °C
 493 ksi
<br>@Temperature 601 °F
 Autoclave Cured; [90°]16
5.30 GPa
<br>@Temperature 177 °C
 769 ksi
<br>@Temperature 351 °F
 Autoclave Cured; [90°]16; Wet condition
7.17 GPa
<br>@Temperature 232 °C
 1040 ksi
<br>@Temperature 450 °F
 Autoclave Cured; [90°]16
7.93 GPa
<br>@Temperature 177 °C
 1150 ksi
<br>@Temperature 351 °F
 Autoclave Cured; [90°]16
9.51 GPa
<br>@Temperature 23.0 °C
 1380 ksi
<br>@Temperature 73.4 °F
 Autoclave Cured; [90°]16
96.46 GPa
<br>@Temperature 232 °C
 13990 ksi
<br>@Temperature 450 °F
 Autoclave Cured; [0°]16; Wet condition
100 GPa
<br>@Temperature 316 °C
 14500 ksi
<br>@Temperature 601 °F
 Autoclave Cured; [0°]16
115.4 GPa
<br>@Temperature 177 °C
 16740 ksi
<br>@Temperature 351 °F
 Autoclave Cured; [0°]16; Wet condition
118.7 GPa
<br>@Temperature 23.0 °C
 17220 ksi
<br>@Temperature 73.4 °F
 Autoclave Cured; [0°]16
120.5 GPa
<br>@Temperature 177 °C
 17480 ksi
<br>@Temperature 351 °F
 Autoclave Cured; [0°]16
129.8 GPa
<br>@Temperature 232 °C
 18830 ksi
<br>@Temperature 450 °F
 Autoclave Cured; [0°]16
Compressive Yield Strength 941.8 MPa
<br>@Temperature 232 °C
 136600 psi
<br>@Temperature 450 °F
 Autoclave Cured; [0°]4
1136 MPa
<br>@Temperature 177 °C
 164800 psi
<br>@Temperature 351 °F
 Autoclave Cured; [0°]4
1282 MPa
<br>@Temperature 232 °C
 185900 psi
<br>@Temperature 450 °F
 Autoclave Cured; [0°]4
1376 MPa
<br>@Temperature 177 °C
 199600 psi
<br>@Temperature 351 °F
 Autoclave Cured; [0°]4
1685 MPa
<br>@Temperature 23.0 °C
 244400 psi
<br>@Temperature 73.4 °F
 Autoclave Cured; [0°]4
Shear Modulus 5.40 GPa
<br>@Temperature 23.0 °C
 783 ksi
<br>@Temperature 73.4 °F
 Autoclave Cured; [+/- 45°]2s
6.10 GPa
<br>@Temperature 177 °C
 885 ksi
<br>@Temperature 351 °F
 Autoclave Cured; [+/- 45°]2s
Shear Strength 34.0 MPa
<br>@Temperature 316 °C
 4930 psi
<br>@Temperature 601 °F
 Short Beam; Autoclave Cured; [0°]16
37.0 MPa
<br>@Temperature 232 °C
 5370 psi
<br>@Temperature 450 °F
 Short Beam; Autoclave Cured; [0°]16; Wet condition
57.0 MPa
<br>@Temperature 177 °C
 8270 psi
<br>@Temperature 351 °F
 Short Beam; Autoclave Cured; [0°]16; Wet condition
68.9 MPa
<br>@Temperature 232 °C
 9990 psi
<br>@Temperature 450 °F
 Short Beam; Autoclave Cured; [0°]16
71.7 MPa
<br>@Temperature 177 °C
 10400 psi
<br>@Temperature 351 °F
 Autoclave Cured; [+/- 45°]2s
88.3 MPa
<br>@Temperature 177 °C
 12800 psi
<br>@Temperature 351 °F
 Short Beam; Autoclave Cured; [0°]16
96.5 MPa
<br>@Temperature 22.0 °C
 14000 psi
<br>@Temperature 71.6 °F
 Autoclave Cured; [+/- 45°]2s
135 MPa
<br>@Temperature 23.0 °C
 19600 psi
<br>@Temperature 73.4 °F
 Short Beam; Autoclave Cured; [0°]16
Descriptive Properties Value Comments
Cured Thickness per Ply (cm) 0.0135-0.0155
Laminate
Dry Resin Content (%) 33-37
Prepreg
Fiber Volume (%) 55-59
Laminate