Mitsubishi Xantar® MX 1020 Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Mitsubishi |
| Trade Name | Xantar® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Mitsubishi Xantar® MX 1020 Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances where quality is a key requirement. The Xantar® range includes: clear and tinted grades for transparent applicationsreinforced materialsFlame retardant and halogen free typeslubricated materials for added wear resistanceMitsubishi Engineering Plastics acquired the Xantar® product line from DSM in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| Water Absorption | 0.35 % | 0.35 % | Sim. to ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4 |
| Melt Flow | 7.08 g/10 min @Load 1.20 kg, Temperature 280 °C |
7.08 g/10 min @Load 2.65 lb, Temperature 536 °F |
Calculated from Volume Flow Rate of 6 cm<sup>3</sup>/10min.; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | ISO 527-1/-2 |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-1/-2 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO 527-1/-2 |
| Tensile Modulus | 2.10 GPa | 305 ksi | ISO 527-1/-2 |
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 60.0 kJ/m² @Temperature -20.0 °C |
28.6 ft-lb/in² @Temperature -4.00 °F |
ISO 180/4A |
| 70.0 kJ/m² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
ISO 180/4A | |
| Dart Drop, Total Energy | 11.0 J @Temperature -30.0 °C |
8.11 ft-lb @Temperature -22.0 °F |
Puncture Energy; ISO 6603-2 |
| 16.0 J @Temperature 23.0 °C |
11.8 ft-lb @Temperature 73.4 °F |
Puncture Energy; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 65.0 µm/m-°C @Temperature 20.0 °C |
36.1 µin/in-°F @Temperature 68.0 °F |
ISO 11359-1/-2 |
| Maximum Service Temperature, Air | 125 °C | 257 °F | Ball Pressure Temperature; IEC 60695-10-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 264 °F | ISO 75-1/-2 |
| Vicat Softening Point | 140 °C | 284 °F | 50°C/h 50N; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 18.0 kV/mm | 457 kV/in | IEC 60243-1 |
| Comparative Tracking Index | 250 - 399 V | 250 - 399 V | PLC 2; UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| High impact or impact modified | Yes | |
| Injection molding | Yes | |
| Release Agent | Yes | |
| Without Fillers | Yes |
Users viewing this material also viewed the following:
- Resinlab® CYNERGY CA6010 Adhesive
- DuPont™ Clysar® HP Polyolefin Shrink Packaging Film, 150 Gauge (discontinued **)
- TPI Porene® KU900 Super High Heat ABS
- Covestro Makroblend® DP 2-7655 Polycarbonate + PET, Mineral Filled Impact Grade
- 3M Scotch® 829 Packing List Pouch Tape
- ATI Allvac® Nickelvac® 625 Nickel Superalloy, Heat Treatment: 927°C (1700°F) Anneal
- BASF Ultramid® A4H PA66 (Dry)
- Resinlab® EP11HTFS Gray Filled Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved