- Polymer Resources TP-IM-G15 Polybutylene Terephthalate, 15% Glass Reinforced, Impact Modified
Polymer Resources TP-IM-G15 Polybutylene Terephthalate, 15% Glass Reinforced, Impact Modified
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled , Polybutylene Terephthalate (PBT), Glass Filled, Impact Modified |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources TP-IM-G15 Polybutylene Terephthalate, 15% Glass Reinforced, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polybutylene Terephthalate, 15% Glass Reinforced, Impact ModifiedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 - 0.010 cm/cm | 0.0060 - 0.010 in/in | ASTM D955 |
| Melt Flow | 8.0 - 16 g/10 min @Load 2.16 kg, Temperature 250 °C |
8.0 - 16 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 82.7 MPa | 12000 psi | ASTM D638 |
| Tensile Strength, Yield | 84.8 MPa | 12300 psi | ASTM D638 |
| Flexural Strength | 128 MPa | 18500 psi | ASTM D790 |
| Flexural Modulus | 4.21 GPa | 610 ksi | ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm @Temperature 22.8 °C |
1.80 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 182 °C | 360 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 238 - 254 °C | 460 - 490 °F | |
| Middle Barrel Temperature | 243 - 260 °C | 470 - 500 °F | |
| Front Barrel Temperature | 249 - 266 °C | 480 - 510 °F | |
| Melt Temperature | 232 - 260 °C | 450 - 500 °F | |
| Mold Temperature | 71.1 - 87.8 °C | 160 - 190 °F | |
| Drying Temperature | 116 - 121 °C | 240 - 250 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0005 |
Users viewing this material also viewed the following:
- Mitsui ADMER® QF500A PP Type Polyolefin
- Lehmann & Voss LUVOCOM® 1105-0895/BL PEEK, with glass fiber
- SABIC Innovative Plastics Noryl TN240 PPE+PS
- A. Schulman POLYFORT™ PP 3719 Impact Copolymer Polypropylene
- Zircar Refractory Composites RS-A1 Refractory Sheet
- Daikin NEOFLON AP-230ASL PFA Pellets
- Aclo Accutech Polypropylene Copolymer CP0437C20L1 Calcium Reinforced
- 3M Scotch® 202 Paper Masking Tape
- 3M Scotchcal™ ElectroCut™ 7725-22 Graphic Film
- Wellman Wellamid® XT1863-BK1 Impact Modified Nylon 66
Copyright © lookpolymers.com All Rights Reserved