- PolyOne Geon™ Vinyl Rigid Extrusion L4230 Polyvinyl Chloride, Rigid (PVC, Rigid)
PolyOne Geon™ Vinyl Rigid Extrusion L4230 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion L4230 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Extrusion capstock for darker colors. This product is not recommended for horizontal, outdoor applications.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 80 | 80 | 10 sec; ASTM D2240 |
| Tensile Strength, Yield | 42.1 MPa | 6110 psi | Type I, 51 mm/min; ASTM D638 |
| Tensile Modulus | 2.24 GPa | 325 ksi | Type I, 51 mm/min; ASTM D638 |
| Flexural Strength | 66.9 MPa | 9700 psi | ASTM D790 |
| Flexural Modulus | 2.34 GPa | 339 ksi | ASTM D790 |
| Izod Impact, Notched | 5.30 J/cm @Temperature -10.0 °C |
9.93 ft-lb/in @Temperature 14.0 °F |
Injection Molded; ASTM D256A |
| 9.60 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
18.0 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 140 µm/m-°C | 77.8 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 76.1 °C @Treatment Temp. 50.0 °C, Thickness 3.18 mm |
169 °F @Treatment Temp. 122 °F, Thickness 0.125 in |
Annealed; ASTM D648 |
| 78.9 °C @Treatment Temp. 60.0 °C, Thickness 3.18 mm |
174 °F @Treatment Temp. 140 °F, Thickness 0.125 in |
Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.8 °C @Thickness 3.18 mm |
163 °F @Thickness 0.125 in |
Compression Molded, Annealed at 50 deg.C; ASTM D648 |
| 77.8 °C @Thickness 3.18 mm |
172 °F @Thickness 0.125 in |
Compression Molded, Annealed at 60 deg.C; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F | |
| 199 - 210 °C | 390 - 410 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Colors Available | |
| Features | High Gloss | |
| High Impact Resistance | ||
| Forms | Cube | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Capstock | |
| Construction Applications | ||
| Outdoor Applications |
Users viewing this material also viewed the following:
- Plastcom SLOVASTER® B1 GF 10 PBT, 10% glass fibre
- Imerys Allenâ„¢ G Kaolin
- SSAB Tunnplat Domex® 044 BOR Rolled Boron Steel
- A. Schulman POLYBLAK™ 3225 Superior Black Color Concentrate, 50% Carbon Black Based In PP Homopolymer
- Eagle Brass 510 Phosphor Bronzes 5% A, 1/4 Hard
- Dow Corning SILASTIC® LC-40-2004 PART A&B KIT
- ELASTO UK Dryflex® 600900S SEBS Based Material, Filled Qualities, 90A Hardness, Natural
- Fainplast Compounds HGK 82 Flexible PVC, Sheathing for High Temperatures Lead Free
- Fainplast Compounds R 316 Rigid PVC, Extrusion
- 3M 1080 Vinyl Film
Copyright © lookpolymers.com All Rights Reserved