LyondellBasell Petrothene® LP510300 High Density Polyethylene, Film Extrusion Grade

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer LyondellBasell (former Equistar)
Trade Name Petrothene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LyondellBasell Petrothene® LP510300 High Density Polyethylene, Film Extrusion Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PETROTHENE LP510300 is a copolymer resin designed for blown film applications. This resin offers high stiffness, excellent appearance and bubble stability and good drawdown. LP510300 is recommended for merchandise bags, and multi-wall sack liners and barrier sheeting. It is also useful as a blend component for improved stiffness and machineability. Regulatory Status: LP510300 meets the requirements of the Food and Drug Administration regulation 21 CFR 177.1520. This regulation allows the use of this olefin polymer in "...articles or components of articles intended for use in contact with food." Specific limitations or conditions of use may apply. Contact your Equistar sales representative for more information. Specific recommendations for processing LP510300 can only be made when the processing conditions, equipment and end use are known. For further suggestions, please contact your Equistar sales representative.This product is from the former Equistar product line.
Physical Properties Metric English Comments
Density 0.949 g/cc
0.0343 lb/in³
ASTM D1505
Water Vapor Transmission 3.30 g/m²/day
0.213 g/100 in²/day
ASTM F372
Oxygen Transmission Rate 2400 cc/m²/day
155 cc/100 in²/day
ASTM D3985
Thickness 50.8 microns
2.00 mil
Melt Flow 0.33 g/10 min
0.33 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 24.8 MPa
3600 psi
ASTM D882
Film Tensile Strength at Yield, TD 28.3 MPa
4100 psi
ASTM D882
Film Elongation at Break, MD 500 %
500 %
ASTM D882
Film Elongation at Break, TD 670 %
670 %
ASTM D882
Elmendorf Tear Strength MD 31 g
31 g
ASTM D1922
Elmendorf Tear Strength TD 1200 g
1200 g
ASTM D1922
Dart Drop 1.38 g/micron
35.0 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 43.4 MPa
6300 psi
ASTM D882
Film Tensile Strength at Break, TD 31.0 MPa
4500 psi
ASTM D882
1% Secant Modulus, MD 758 MPa
110000 psi
ASTM E111
1% Secant Modulus, TD 924 MPa
134000 psi
ASTM E111
Thermal Properties Metric English Comments
Vicat Softening Point 126 °C
259 °F
ASTM D1525
Processing Properties Metric English Comments
Melt Temperature 199 - 210 °C
390 - 410 °F
Die Opening 0.1524 cm
0.06000 in
Blow-up Ratio (BUR) 2.5
2.5