Cossa Polimeri ESTAPROP H 2550 CBS/E Polypropylene, 25% Mineral Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTAPROP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTAPROP H 2550 CBS/E Polypropylene, 25% Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PP homopolymer 25% mineral fillerHigh gloss, very high melt flow rate, excellent processabilityInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.011 - 0.013 cm/cm | 0.011 - 0.013 in/in | ASTM D 955 |
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 230 °C |
30 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 23.0 MPa | 3340 psi | ASTM D 638 |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ASTM D 638 |
| Elongation at Break | 50 % | 50 % | ASTM D 638 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ASTM D 638 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.150 J/cm @Temperature -20.0 °C |
0.281 ft-lb/in @Temperature -4.00 °F |
ASTM D 638 |
| 0.250 J/cm @Temperature 0.000 °C |
0.468 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 | |
| 0.350 J/cm @Temperature 23.0 °C |
0.656 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | 120°C/hr; ASTM D 648 |
| Vicat Softening Point | 95.0 °C @Load 5.00 kg |
203 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
Users viewing this material also viewed the following:
- Pau Tai UNISTAB EC-295 Stabilizers for Cable
- Gromax BFG30-AH00B3 Nylon 6 30% Glass Filled (Conditioned)
- Styron Pulse® 1550 ABS + Polycarbonate, 10% Glass Reinforced
- A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene
- Zotefoams Plastazote® LD15FMSV Low Density Polyethylene Foam, Flame Retarded
- 3M Scotch® 824 Pouch Tape
- Arlon R38041X012 0.012" (0.305 mm) Uncured Fluorosilicone with Fiberglass Substrate
- Overview of materials for Ethylene-Methyl Acrylate Copolymer, Compounding Grade
- ChevronTexaco HDAX® SAE 40 Ashless Gas Engine Oil
Copyright © lookpolymers.com All Rights Reserved