LyondellBasell Higlass SB224-2 Polypropylene Copolymer, 20% Glass Fiber
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | LyondellBasell |
| Trade Name | Higlass |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Higlass SB224-2 Polypropylene Copolymer, 20% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Features: conventional melt flow, medium modulus, chemically coupled, glass fiber-reinforced polypropylene copolymer, high impact strength, moderate rigidity, good processabilityApplications: office equipment components, lawn equipment housings, splice enclosuresDescription: Higlass SB224-2 conventional melt flow, chemically coupled, 20% glass fiber-reinforced polypropylene copolymer has an excellent balance of strength, stiffness and impact resistance.Information provided by Montell Polyolefins.LyondellBasell is the successor company to Montell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | Tool, Montell |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | ASTM D638 |
| Elongation at Break | 8.0 % | 8.0 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Modulus | 2.60 GPa | 377 ksi | Tangent at 0.05 in/min; ASTM D790A |
| Izod Impact, Notched | 2.10 J/cm | 3.93 ft-lb/in | ASTM D256A |
| Izod Impact, Unnotched | 6.40 J/cm | 12.0 ft-lb/in | ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | ASTM D648 |
| UL RTI, Mechanical with Impact | 110 °C @Thickness 1.60 mm |
230 °F @Thickness 0.0630 in |
|
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Users viewing this material also viewed the following:
- SABIC MG200024 Linear Low Density Polyethylene for Compounding
- NIZHNEKAMSKNEFTEKHIM PP 1500M (X30G) Propylene Homopolymer
- PolyOne Elastamax™ HTE 1104 Styrene Butadiene Block Copolymer (SBC) (discontinued **)
- Mueller Dynalloy Alloy 6730 Free cutting bearing bronze (UNS C67300)
- A. Schulman INVISION™ VX-5075UI Soft Touch Polyolefin Thermoplastic
- Polyplastics Duranex® 3300H Polybutylene Terephthalate (PBT), Standard, 30% GF filled
- A. Schulman SCHULAMID® 66 GF33HS 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- DSM Arnitel® PL650 Polyether Ester Elastomer (European and Asian Grade)
- 3M Jet-Weld™ TS-230 Adhesive
Copyright © lookpolymers.com All Rights Reserved