- LyondellBasell Hifaxâ„¢ CB247G Thermoplastic Polyolefin Elastomer
LyondellBasell Hifaxâ„¢ CB247G Thermoplastic Polyolefin Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin |
| Manufacturer | LyondellBasell |
| Trade Name | Hifax™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hifaxâ„¢ CB247G Thermoplastic Polyolefin Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Hifaxâ„¢ CB247G high melt flow, 1,700 MPa flexural modulus, UV-stabilized, weatherable, mineral-filled thermoplastic elastomeric olefin (TEO) resin has a very good balance of properties and processability. It was designed for selected automotive interior and exterior components. Uses: Automotive applicationsInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 230 °C |
13 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO 527-1, -2 |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | ISO 527-1, -2 |
| Elongation at Break | 80 % | 80 % | ISO 527-1, -2 |
| Elongation at Yield | 7.0 % | 7.0 % | ISO 527-1, -2 |
| Flexural Modulus | 1.70 GPa | 247 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.20 kJ/m² @Temperature -40.0 °C |
1.52 ft-lb/in² @Temperature -40.0 °F |
ISO 180 |
| 26.0 kJ/m² @Temperature 23.0 °C |
12.4 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Dart Drop, Total Energy | 18.0 J @Temperature 23.0 °C |
13.3 ft-lb @Temperature 73.4 °F |
Instrumented Energy at Maximum Load, Ductile Failure; ASTM D3763 |
| 23.0 J @Temperature -15.0 °C |
17.0 ft-lb @Temperature 5.00 °F |
Instrumented Energy at Maximum Load, Ductile Failure; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 56.0 µm/m-°C @Temperature -30.0 - 100 °C |
31.1 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C | 217 °F | Unannealed; ISO 75B-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | Unannealed; ISO 75A-1, -2 |
| Shrinkage | 0.80 % | 0.80 % | Tool, 100x150x3.2 mm; Basell Test Method |
| 1.10 % @Temperature 121 °C, Time 3600 sec |
1.10 % @Temperature 250 °F, Time 1.00 hour |
Afterbake, 100x150x3.2 mm; Basell Method |
Users viewing this material also viewed the following:
- Nylene® PA6 Glass/Mineral Filled 7115 HS Nylon 6
- ExxonMobil Escorene® LD-767 High EVA Film and Compounding Resin (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP RAL23S PA 66 (Europe-Africa-Middle East)
- A. Schulman POLYBATCH™ Brown 1281 Concentrate Based In Polyethylene
- Dow LDPE 752A Low Density Polyethylene, Film Grade
- Asahi Kasei Tenac®-C 7554 Copolymer Acetal Resin
- Ametek P303L P/M Stainless Steel, Sintered from 6.7 g/cc Green Density
- Axiall 3803 Vinyl Foam, Extrusion
- SABIC Innovative Plastics Lexan® HFD4413 PC (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved