Lucite International Diakon® Frost 952 51 Acrylic Polymer
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, General Purpose, Molded |
| Manufacturer | Lucite International |
| Trade Name | Diakon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucite International Diakon® Frost 952 51 Acrylic Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Lucite International
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | ISO 62 |
| Melt Flow | 1.3 g/10 min | 1.3 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 94 | 94 | ISO 2039-2 |
| Ball Indentation Hardness | 180 MPa | 26100 psi | ISO 2039-1 (H 961-30) |
| Tensile Strength | 73.0 MPa | 10600 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Flexural Strength | 103 MPa | 14900 psi | ISO 178 |
| Flexural Modulus | 3.40 GPa | 493 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 1.60 kJ/m² | 0.761 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.140 J/cm² | 0.666 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75B |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ISO 75A |
| Vicat Softening Point | 102 °C | 216 °F | ISO 306B |
| 109 °C | 228 °F | ISO 306A | |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | IEC 695-2-1 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 66 % | 66 % | ASTM D1003 |
| Transmission, Visible | 74 % | 74 % | ASTM D1003 |
Users viewing this material also viewed the following:
- Polymer Resources PPX-SF1 Modified-PPO, Structural Foam Grade, Flame Retardant, Easy Flow
- Phillips 66 COPYLENE® CM020N Polypropylene Impact Copolymer
- H.C. Starck Amperit® 584.072 Chromium Carbide-Nickel-Chromium 75-25 (Cr3C2-NiCr)
- Lushan EV1050G1 EVA Film for Encapsulating Solar modules, Ultra Fast Cure
- Universal Wire Works ER308L Stainless Steel Bare Wire
- A. Schulman POLYBATCH™ Blue 40460/4 Concentrate Based In LLDPE
- Covestro Baydur® STR/C-405 IMR Polyurethane Composite SRIM Foam, 45% Glass Filled, MDI-based 2-Component Liquid System
- ChevronTexaco 260 Compressor Oil
- Beijing Ranger Chem PBT-MFC-G20 FR PBT
- Bulk Molding Compounds tetra-DUR F 4308 Bulk Molding Compound
Copyright © lookpolymers.com All Rights Reserved