- Cossa Polimeri ESTAPROP 0540 GFC V0 Flame Retardant Polypropylene, 20% Glass Filled
Cossa Polimeri ESTAPROP 0540 GFC V0 Flame Retardant Polypropylene, 20% Glass Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler , Polypropylene, Flame Retardant |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTAPROP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTAPROP 0540 GFC V0 Flame Retardant Polypropylene, 20% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PP with 20% chemically coupled glass fiberFlame retardant class V0, excellent mechanical characteristics, excellent heat resistanceInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ASTM D 955 |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | ASTM D 638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D 638 |
| Flexural Modulus | 5.00 GPa | 725 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.400 J/cm @Temperature 0.000 °C |
0.749 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 |
| 0.500 J/cm @Temperature 23.0 °C |
0.937 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | 120°C/hr; ASTM D 648 |
| Vicat Softening Point | 120 °C @Load 5.00 kg |
248 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| Glow Wire Test | 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
I.E.C. 695-2-1 |
Users viewing this material also viewed the following:
- Nye Lubricants 368AX-F (RL) Synthetic Oil
- Radici Radilon® S CP300 (dry) Nylon 6
- Polimeri Europa Extir® CM Giotto 5 AE Expandable Polystyrene - Continuous Mass/Flame Retardant
- SABIC Innovative Plastics Lexan® 955 PC
- Momentive Performance Materials RTV5223 Black Adhesive Sealant, Low Modulus Paste
- Momentive Performance Materials Siloprenâ„¢ LIM 8040 Liquid Silicone Rubber - Self-Bonding
- Constellium PLAN OX 5754 Aluminum Rolled Plate
- Chevron Phillips MarFlex® 5429 Low Density Polyethylene, Cast Film
- 3M QI-5/16-220 Cold Shrink Quick Insulator
- Polykemi AB POLYfill PPC 15000 Polypropylene Copolymer
Copyright © lookpolymers.com All Rights Reserved