- HOME
- POLYMER SEARCH
- Thermoplastic
- Polypropylene (PP)
- Polypropylene with 40% Glass Fiber Filler
- Asahi Kasei Thermylene® P7-40FG-0790 40% Glass Fiber Reinforced, Heat Stabilized
Asahi Kasei Thermylene® P7-40FG-0790 40% Glass Fiber Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Glass Fiber Filler |
| Manufacturer | Asahi Kasei |
| Trade Name | Thermylene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Thermylene® P7-40FG-0790 40% Glass Fiber Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asahi Thermofil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 116 | 116 | ASTM D785 |
| Tensile Strength, Yield | 110 MPa | 16000 psi | ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | ASTM D638 |
| Tensile Modulus | 10.3 GPa | 1500 ksi | ASTM D638 |
| Flexural Strength | 152 MPa | 22000 psi | ASTM D790 |
| Flexural Modulus | 7.31 GPa | 1060 ksi | ASTM D790 |
| Izod Impact, Notched | 1.12 J/cm | 2.10 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.94 J/cm | 13.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 25.2 µm/m-°C @Temperature 20.0 °C |
14.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 154 °C | 310 °F | ASTM D648 |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Rynite® FR530 BK507 PET (Unverified Data**)
- Lehmann & Voss LUVOCOM® 19-7744 Polyamide 46, with aramid reinforcement and PTFE
- SABIC Innovative Plastics LNP THERMOCOMP WF006U PBT (Asia Pacific)
- Sumitomo Bakelite Durez® 29502 Phenolic, Compression Grade
- A. Schulman POLYBATCH™ Bright Pink 50379 Concentrate Based In Polyethylene
- Zig Sheng Industrial ZISAMIDE® TP6603 Nylon 6
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 0.25 PHR Thanecure ZM
- DSM Biomedical Elasthane™ 55D Thermoplastic Polyether Polyurethane (TPU)
- Dow AMPLIFY™ VA 400 Ethylene vinyl acetate (EVA)
Copyright © lookpolymers.com All Rights Reserved