Lubrizol Estane® 2103-55D Thermoplastic Polyurethane Elastomer

Category	Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade
Manufacturer	Lubrizol (former Noveon)
Trade Name	ESTANE®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lubrizol Estane® 2103-55D Thermoplastic Polyurethane Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Formerly PellethaneFeature: Load bearing capacityAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product line from Dow in 2009.

Physical Properties	Metric	English	Comments
Density	1.15 g/cc	0.0415 lb/in³	ASTM D792
Linear Mold Shrinkage, Flow	0.0060 - 0.0070 cm/cm	0.0060 - 0.0070 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0050 - 0.0090 cm/cm	0.0050 - 0.0090 in/in	ASTM D955
Melt Flow	15 g/10 min @Load 0.160 kg, Temperature 224 °C	15 g/10 min @Load 0.353 lb, Temperature 435 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	96	96	ASTM D2240
Hardness, Shore D	55	55	ASTM D2240
Tensile Strength, Ultimate	44.1 MPa	6400 psi	ASTM D412
Elongation at Break	425 %	425 %	ASTM D412
50% Modulus	0.0134 GPa	1.94 ksi	ASTM D412
100% Modulus	0.0165 GPa	2.39 ksi	ASTM D412
300% Modulus	0.0317 GPa	4.60 ksi	ASTM D412
Flexural Modulus	0.172 GPa	24.9 ksi	ASTM D412
Tear Strength	158 kN/m	902 pli	Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles	80	80	H22 Wheel, 1000 g; ASTM D1044
Compression Set	25 % @Temperature 25.0 °C, Time 79200 sec	25 % @Temperature 77.0 °F, Time 22.0 hour	ASTM D395, Method B
	30 % @Temperature 70.0 °C, Time 79200 sec	30 % @Temperature 158 °F, Time 22.0 hour	ASTM D395, Method B
Tensile Set	30 %	30 %	Elongation set after break; ASTM D412

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	130 µm/m-°C @Temperature 20.0 °C	72.2 µin/in-°F @Temperature 68.0 °F	ASTM D696
Vicat Softening Point	104 °C	219 °F	120°C/hr, 9.8N; ASTM D1525

Processing Properties	Metric	English	Comments
Melt Temperature	210 - 227 °C	410 - 441 °F	Molding
Mold Temperature	16.0 - 60.0 °C	60.8 - 140 °F
Drying Temperature	88.0 - 104 °C	190 - 219 °F	air dew point <-40°C