Loxim 820 12 HB Polypropylene Compound, Flame Retardant
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | Loxim Industries |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Loxim 820 12 HB Polypropylene Compound, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Loxim Industries
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.00 - 1.10 g/cc | 1.00 - 1.10 g/cc | ASTM D792 |
| Filler Content | 20 % | 20 % | |
| Linear Mold Shrinkage | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | ASTM D1299 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 38.0 - 42.0 MPa | 5510 - 6090 psi | ASTM D683 |
| Elongation at Break | 8.0 - 12 % | 8.0 - 12 % | ASTM D638 |
| Flexural Modulus | 2.80 - 3.20 GPa | 406 - 464 ksi | ASTM D790 |
| Izod Impact, Notched | 0.400 - 0.500 J/cm | 0.749 - 0.937 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 120 - 130 °C | 248 - 266 °F | ASTM D1525, HDT Method B |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA - 51 HF OG General Purpose Acrylic Resin
- Gromax BFM30-EL03N1 Nylon 6 30% Mineral Filled (Conditioned)
- LATI Laticonther 83 CP/80 PA12, Impact Modified
- Taiwan PU Corporation TPUI-L75 Low Temperature Resistance, Injection Molding Polyester Base TPU
- Saint-Gobain CHR® SG55-03(R) Anti-Static Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- Eastman Eastar MN052 Polyester, Natural
- Fainplast Compounds GS 61 Flexible PVC, Injection Molding for Footwear
- Aclo Accutech Polypropylene CP0435G20HIV Copolymer Glass Reinforced High Impact
- DuPont Performance Polymers Hytrel® 5526 Polyester Elastomer TPC-ET (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved