Akro-Plastic Akromid® A3 GF 60 (2424) PA 6.6 Conditioned, 60% Glass Filled

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 60% Glass Fiber Filled
Manufacturer	Akro-Plastic
Trade Name	Akromid®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Akro-Plastic Akromid® A3 GF 60 (2424) PA 6.6 Conditioned, 60% Glass Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatures as well as easy processing. AKROMID® A is an engineering plastic compound that allows a broad range of possible applications. On the basis of these standard types, we are able to develop individual compounds for special application needs.Information from Akro-Plastic

Physical Properties	Metric	English	Comments
Density	1.71 g/cc	0.0618 lb/in³	ISO 1183
Filler Content	60 %	60 %	ISO 1172
Water Absorption	1.0 - 1.2 % @Temperature 70.0 °C	1.0 - 1.2 % @Temperature 158 °F	62% r.h., Humidity; ISO 62
Water Absorption at Saturation	3.2 - 3.7 % @Time 82800 sec	3.2 - 3.7 % @Time 23.0 hour	ISO 62
Linear Mold Shrinkage, Flow	0.0040 cm/cm	0.0040 in/in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.0080 cm/cm	0.0080 in/in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	190 MPa	27600 psi	5 [mm/min]; ISO 527-1/2
Elongation at Break	2.5 %	2.5 %	5 [mm/min]; ISO 527-1/2
Tensile Modulus	15.8 GPa	2290 ksi	1[mm/min]; ISO 527-1/2
Charpy Impact Unnotched	10.5 J/cm² @Temperature 23.0 °C	50.0 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	2.20 J/cm² @Temperature 23.0 °C	10.5 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	262 °C	504 °F	ISO 11357-1/3

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+10 ohm-cm	1.00e+10 ohm-cm	IEC 60093
Surface Resistance	1.00e+10 ohm	1.00e+10 ohm	IEC 60093