Solvay Specialty Polymers AvaSpire® AV-722 Polyaryletherketone (PAEK)
| Category | Polymer , Thermoplastic , Polyketone |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | AvaSpire® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers AvaSpire® AV-722 Polyaryletherketone (PAEK).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AvaSpire® AV-722 is an unreinforced polyaryletherketone (PAEK) that offers improved economics relative to PEEK while retaining most of PEEK's key performance attributes. AV-722 resin has been formulated for applications requiring high chemical resistance and mechanical strength along with low moisture absorption and good barrier properties. These and other properties make this resin well-suited for applications in healthcare, transportation, electronics, chemical processing and other industries.Features: Ductile; Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; Good Impact Resistance; High Heat ResistanceUses: Aircraft Applications; Automotive Applications; Electrical/Electronic Applications; Film; Fuel Lines; Gears; Medical/Healthcare Applications; Oil/Gas Applications; SealsInjection Molding Notes: Back Pressure: MinimumInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ASTM D792 |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ISO 62 |
| Viscosity | 450000 cP @Shear Rate 1000 1/s, Temperature 400 °C |
450000 cP @Shear Rate 1000 1/s, Temperature 752 °F |
Melt Viscosity; ASTM D3835 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.010 cm/cm @Thickness 3.18 mm |
0.0080 - 0.010 in/in @Thickness 0.125 in |
|
| Linear Mold Shrinkage, Transverse | 0.012 - 0.014 cm/cm @Thickness 3.18 mm |
0.012 - 0.014 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 400 °C |
1.0 g/10 min @Load 4.76 lb, Temperature 752 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 95 | 95 | ASTM D785 |
| Tensile Strength | 89.0 MPa | 12900 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 91.0 MPa | 13200 psi | Type 1A, 50 mm/min; ISO 527-2 |
| Elongation at Break | 25 % | 25 % | Type 1A, 50 mm/min; ISO 527-2 |
| 25 % | 25 % | 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.5 % | 4.5 % | Type 1A, 50 mm/min; ISO 527-2 |
| 5.0 % | 5.0 % | 50 mm/min; ASTM D638 | |
| Tensile Modulus | 3.70 GPa | 537 ksi | 50 mm/min; ASTM D638 |
| 3.90 GPa | 566 ksi | 1 mm/min, Type 1A; ISO 527-2 | |
| Flexural Strength | 138 MPa | 20000 psi | ISO 178 |
| 141 MPa | 20500 psi | ASTM D790 | |
| Flexural Modulus | 3.70 GPa | 537 ksi | ASTM D790 |
| 3.80 GPa | 551 ksi | ISO 178 | |
| Compressive Strength | 112 MPa | 16200 psi | ASTM D695 |
| Poissons Ratio | 0.43 | 0.43 | ASTM E132 |
| Shear Strength | 79.0 MPa | 11500 psi | ASTM D732 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 45.0 µm/m-°C @Temperature -50.0 - 50.0 °C |
25.0 µin/in-°F @Temperature -58.0 - 122 °F |
1 |
| Specific Heat Capacity | 1.41 J/g-°C @Temperature 50.0 °C |
0.337 BTU/lb-°F @Temperature 122 °F |
ASTM C351 |
| 1.97 J/g-°C @Temperature 200 °C |
0.471 BTU/lb-°F @Temperature 392 °F |
ASTM C351 | |
| Thermal Conductivity | 0.220 W/m-K | 1.53 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 340 °C | 644 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 161 °C @Thickness 3.20 mm |
322 °F @Thickness 0.126 in |
Annealed; ASTM D648 |
| Glass Transition Temp, Tg | 150 °C | 302 °F | DSC |
| Oxygen Index | 40 % | 40 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3.10e+17 ohm-cm | 3.10e+17 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.90e+17 ohm | >= 1.90e+17 ohm | ASTM D257 |
| Dielectric Constant | 3.12 @Frequency 1.00e+6 Hz |
3.12 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 170 kV/mm @Thickness 3.00 mm |
4320 kV/in @Thickness 0.118 in |
ASTM D149 |
| Dissipation Factor | 0.0010 @Frequency 60.0 Hz |
0.0010 @Frequency 60.0 Hz |
ASTM D150 |
| 0.0040 @Frequency 1.00e+6 Hz |
0.0040 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 354 °C | 669 °F | |
| Middle Barrel Temperature | 366 °C | 691 °F | |
| Front Barrel Temperature | 371 °C | 700 °F | |
| Nozzle Temperature | 374 °C | 705 °F | |
| Mold Temperature | 177 - 204 °C | 351 - 399 °F | |
| Drying Temperature | 149 °C @Time 14400 sec |
300 °F @Time 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Beige | |
| Form | Pellets | |
| Injection Rate | Fast | |
| Processing Technique | Extrusion Blow Molding | |
| Fiber (Spinning) Extrusion; Film Extrusion | ||
| Injection Blow Molding; Injection Molding | ||
| Machining; Profile Extrusion | ||
| Thermoforming; Wire & Cable Extrusion | ||
| Screw Compression Ratio | 2.5:1.0 to 3.5:1.0 |
Users viewing this material also viewed the following:
- Silberline SparkleBriteâ„¢ 190NL-PA
- Styron CALIBREâ„¢ 7100-15 Polycarbonate
- SABIC Innovative Plastics LNP THERMOCOMP RF00CSXZ PA 66
- TIMCAL TIMREX® KC44 Primary Synthetic Graphite
- A. Schulman POLYBATCH™ Orange 1046E Concentrate Based In Polyethylene
- Tisan TISAKRIL® UNR ABS
- Dow Corning SYL-OFF® PMCP7923 Catalyst Emulsion
- BASF Palatinol® TNTM Tri Isononyl Trimellitate
- Advanced Polymer Alloys Alcryn® 2060 BK Melt Processable Rubber
Copyright © lookpolymers.com All Rights Reserved