Lehmann & Voss LUVOCOMÂ® TPE-0900 VP Thermoplastic elastomer, with carbon fiber

Category	Polymer , Thermoplastic , Elastomer, TPE
Manufacturer	Lehmann & Voss & Co.
Trade Name	LUVOCOM®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lehmann & Voss LUVOCOMÂ® TPE-0900 VP Thermoplastic elastomer, with carbon fiber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Applications: Electrically conductive, suitable for continuous discharging of statically generated electricity.Improved wear behaviour, low warpage.Bearings, sleeves, sliding elements, chair rollers, handles.Information provided by Lehmann & Voss & Co.KG

Physical Properties	Metric	English	Comments
Specific Gravity	1.26 g/cc	1.26 g/cc	ISO 1183
Water Absorption	<= 0.50 %	<= 0.50 %	23Â°C/24h
Linear Mold Shrinkage	0.0040 - 0.0080 cm/cm	0.0040 - 0.0080 in/in

Mechanical Properties	Metric	English	Comments
Tensile Stress	40.0 MPa	5800 psi
Elongation at Yield	7.0 %	7.0 %
	9.5 %	9.5 %	flexural
Modulus of Elasticity	1.60 GPa	232 ksi
Flexural Strength	55.0 MPa	7980 psi
Flexural Modulus	1.30 GPa	189 ksi

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	80.0 Â°C	176 Â°F
	110 Â°C	230 Â°F	short term

Electrical Properties	Metric	English	Comments
Surface Resistance	<= 1.00e+6 ohm	<= 1.00e+6 ohm
Insulation Resistance	<= 1.00e+6 ohm	<= 1.00e+6 ohm

Processing Properties	Metric	English	Comments
Processing Temperature	210 Â°C	410 Â°F	mass temp
Nozzle Temperature	200 - 220 Â°C	392 - 428 Â°F
Zone 1	185 - 205 Â°C	365 - 401 Â°F
Zone 2	190 - 210 Â°C	374 - 410 Â°F
Zone 3	195 - 215 Â°C	383 - 419 Â°F
Mold Temperature	25.0 - 55.0 Â°C	77.0 - 131 Â°F
Drying Temperature	85.0 Â°C @Time 7200 - 10800 sec	185 Â°F @Time 2.00 - 3.00 hour	Dehumidifying dryer

Descriptive Properties	Value	Comments
Color	natural color (black)