SABIC Innovative Plastics Lexan® ML1010 PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® ML1010 PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Superior performance, improved flow over standard grades at lower temperatures. Internal mold release.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Melt Flow | 12 g/10 min @Load 1.20 kg, Temperature 250 °C |
12 g/10 min @Load 2.65 lb, Temperature 482 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 48 g/10 min @Load 1.20 kg, Temperature 300 °C |
48 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 100 MPa | 14500 psi | ISO 2039-1 |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 70 % | 70 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.35 GPa | 341 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 120 °C | 248 °F | Rate B/50; ISO 306 |
| 122 °C | 252 °F | Rate B/120; ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.582 | 1.582 | ISO 489 |
| Haze | 1.0 % @Thickness 2.54 mm |
1.0 % @Thickness 0.100 in |
ASTM D 1003 |
| Transmission, Visible | 88 % @Thickness 2.54 mm |
88 % @Thickness 0.100 in |
ASTM D 1003 |
Users viewing this material also viewed the following:
- Proto3000 Objet VeroBlue FullCure840 Rigid Opaque Prototyping Polymer
- Nilit FRIANYL B63 V2 Nylon 6.6 for injection molding
- NOVA Chemicals DYLARK® 250 Impact Grade Engineering Resin
- Overview of materials for Polyphenylene Sulfide (PPS) with PTFE Filler
- SABIC Innovative Plastics PC2200R PC (Europe-Africa-Middle East)
- Tisan TISLAMID® 66 30% Glass Fiber Reinforced Nylon 66
- ChevronTexaco Regal® EP 46
- E-Polymers TEKANATE™ G715FR , Flame Retardant, 15% Glass Fiber Reinforced Poly Carbonate
- Huntsman PE7011 Profile Extrusion Polyethylene (discontinued **)
- Shin-Etsu Silicones SPD-T5 Fluid
Copyright © lookpolymers.com All Rights Reserved