Lehmann & Voss LUVOCOM® 80-7919 Polyacetal-copolymer, with PTFE, easy flowing
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, PTFE Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 80-7919 Polyacetal-copolymer, with PTFE, easy flowing.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Emergency running property, glide mating with low sliding friction.Bearings, sleeves, control disks, gear wheels, cams.No mass temperature above 215°C! Ventilation of machinery is recommended.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ISO 1183 |
| Water Absorption | 0.15 % | 0.15 % | 23°C/24h |
| Linear Mold Shrinkage | 0.018 - 0.026 cm/cm | 0.018 - 0.026 in/in | |
| Melt Flow | 49.17 g/10 min @Load 2.16 kg, Temperature 190 °C |
49.17 g/10 min @Load 4.76 lb, Temperature 374 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 45.0 MPa | 6530 psi | |
| Elongation at Yield | 7.5 % | 7.5 % | |
| 10 % | 10 % | flexural | |
| Modulus of Elasticity | 2.20 GPa | 319 ksi | |
| Flexural Strength | 65.0 MPa | 9430 psi | |
| Flexural Modulus | 1.80 GPa | 261 ksi | |
| Charpy Impact Unnotched | 3.60 J/cm² | 17.1 ft-lb/in² | edgewise; ISO 179 1eU |
| 3.40 J/cm² @Temperature -30.0 °C |
16.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179 1eA |
| 0.250 J/cm² @Temperature -30.0 °C |
1.19 ft-lb/in² @Temperature -22.0 °F |
ISO 179 eA | |
| Coefficient of Friction, Dynamic | 0.16 | 0.16 | |
| Coefficient of Friction, Static | 0.080 | 0.080 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| 120 °C | 248 °F | short term | |
| Vicat Softening Point | 145 °C | 293 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 °C | 392 °F | mass temp |
| Nozzle Temperature | 175 - 200 °C | 347 - 392 °F | |
| Zone 1 | 175 - 190 °C | 347 - 374 °F | |
| Zone 2 | 185 - 205 °C | 365 - 401 °F | |
| Zone 3 | 180 - 200 °C | 356 - 392 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 7200 - 28800 sec |
167 °F @Time 2.00 - 8.00 hour |
Dehumidifying dryer |
| 120 °C @Time 7200 - 14400 sec |
248 °F @Time 2.00 - 4.00 hour |
Air-Circulation Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (white) |
Users viewing this material also viewed the following:
- Polymer Resources NY66-IM2 Impact Modified Nylon 66
- Momentive Performance Materials IS803 Black Adhesive Sealant, General Purpose Paste
- LG Chemical 80HF SAN, High Transparency, Heat Resistance, Chemical Resistance
- Plenco 6990 Phenolic, Briquette, Injection Molded
- Tra-Con Tra-Bond 2114 Water White Transparent Epoxy Adhesive
- UBE 7034T Nylon 6/12 Monofilament (Drawing Ratio=4.5, Diameter 2 mm)
- BASF Ultramid® A3G5 25% Glass Filled PA66 (Dry)
- Ashley Polymers Ashlene® 265 PPO, 20% Glass Reinforced
- PolyOne Synplast™ DOA-N Di (2-ethylhexyl) Adipate
- CeramTec B 40 Alumina, 99.1%
Copyright © lookpolymers.com All Rights Reserved