SCG Chemicals EL-Proâ„¢ P842J Polypropylene Injection Molding
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | SCG Chemicals Co. |
| Trade Name | EL-Pro™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SCG Chemicals EL-Proâ„¢ P842J Polypropylene Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Characteristics:Excellent flowabilityExcellent processabilityExcellent stiffnessSuitable for complex parts and large partsRecommended Applications:Electrical appliance parts, mainly for refrigerator parts and washing machine parts, e.g. base, tub, control panelInformation provided by SCG Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.910 g/cc | 0.910 g/cc | ASTM D1505 |
| Linear Mold Shrinkage, Flow | 0.0144 cm/cm @Thickness 2.00 mm |
0.0144 in/in @Thickness 0.0787 in |
TPE Method |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm @Thickness 2.00 mm |
0.013 in/in @Thickness 0.0787 in |
TPE Method |
| Melt Flow | 40 g/10 min @Load 2.16 kg, Temperature 230 °C |
40 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 80 | 80 | ASTM D785 |
| Tensile Strength at Break | 18.0 MPa | 2610 psi | ASTM D638 |
| Tensile Strength, Yield | 28.9 MPa | 4200 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Flexural Modulus | 1.42 GPa | 206 ksi | ASTM D790 |
| Izod Impact, Notched | 0.343 J/cm @Temperature -20.0 °C |
0.643 ft-lb/in @Temperature -4.00 °F |
ASTM D256 |
| 0.441 J/cm @Temperature 0.000 °C |
0.827 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| 0.588 J/cm @Temperature 23.0 °C |
1.10 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 163 °C | 325 °F | ASTM D2117 |
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| Vicat Softening Point | 150 °C | 302 °F | ASTM D1525 |
| Brittleness Temperature | -20.0 °C | -4.00 °F | ASTM D746 |
| Flammability, UL94 | HB | HB |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 80 % @Thickness 1.00 mm |
80 % @Thickness 0.0394 in |
ASTM D1003 |
| Gloss | 30 % @Thickness 1.00 mm |
30 % @Thickness 0.0394 in |
ASTM D2457 |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM PE 4142L (424F5) High Density Polyethylene
- ExxonMobil Santoprene® 121-65M300 Thermoplastic Elastomer (discontinued **)
- Lanxess Durethan® BKV 215 000000 Nylon 6-Copolymer, Glass Fiber Reinforced, Impact Modified
- Shinil Chemical SHINCON PES Electro Conductive Polymer
- Samyang Triloy® 215 PC/ABS alloy
- Polyram Polytron P50B07 Polypropylene, 50% Long Glass Fiber, UV Stabilized
- ExxonMobil HDPE HMA 014 High Density Polyethylene Resin
- Ascend Performance Materials Vydyne® R228 Nylon 66, 40% Mineral Reinforced, Conditioned
Copyright © lookpolymers.com All Rights Reserved