- Lehmann & Voss LUVOCOM® 7/CF/30/BK Polyamide 610, with carbon fiber
Lehmann & Voss LUVOCOM® 7/CF/30/BK Polyamide 610, with carbon fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 610 , Nylon 610, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 7/CF/30/BK Polyamide 610, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Especially suitable at dynamic stress situations.Electrically conductive, suitable for continuous discharging of statically generated electricity.Low waterabsorbtion, for dimensional stable precision parts.Bearings, sleeves, sliding elements, handles, machine parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ISO 1183 |
| Water Absorption | <= 0.15 % | <= 0.15 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 210 MPa | 30500 psi | |
| Elongation at Yield | 2.0 % | 2.0 % | |
| 2.6 % | 2.6 % | flexural | |
| Modulus of Elasticity | 20.0 GPa | 2900 ksi | |
| Flexural Strength | 305 MPa | 44200 psi | |
| Flexural Modulus | 16.0 GPa | 2320 ksi | |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | edgewise; ISO 179 1eU |
| 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | ISO 179 1eA |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179 eA | |
| Coefficient of Friction, Dynamic | 0.26 | 0.26 | |
| Coefficient of Friction, Static | 0.20 | 0.20 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 16.0 µm/m-°C | 8.89 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.500 W/m-K | 3.47 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |
| 140 °C | 284 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 100 ohm | <= 100 ohm | |
| Insulation Resistance | <= 1000 ohm | <= 1000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 265 °C | 509 °F | mass temp |
| Nozzle Temperature | 270 - 290 °C | 518 - 554 °F | |
| Zone 1 | 240 - 270 °C | 464 - 518 °F | |
| Zone 2 | 260 - 280 °C | 500 - 536 °F | |
| Zone 3 | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 36000 sec |
167 °F @Time 6.00 - 10.0 hour |
Dehumidifying dryer |
| 105 °C @Time <=14400 sec |
221 °F @Time <=4.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Formosa Plastics Formolene® E904 Film HDPE (discontinued **)
- DuPont Selar® RB 421 EVOH Barrier Resin (discontinued **)
- Kolon KOPA® KN177N Nylon Extrusion Resin
- Sylvin Technologies 9600-60 Clear PVC Molding Compound
- DuPont Appeel® LSR20D752 Lidding Sealant Resin
- Dow ELITE™ 5500G Enhanced Polyethylene Resin
- DuPont Teijin Films Melinex® ST506 Polyester Film, 700 Gauge
- Ascend Performance Materials Vydyne® R530H NAT Nylon 66, 30% Glass Reinforced, Conditioned
- C.O.I.M. LARIPUR® LPR9060 PTMG Polyether Polyurethane
Copyright © lookpolymers.com All Rights Reserved