Lehmann & Voss LUVOCOM® 6/CF/30 Polyamide 12, with carbon fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 6/CF/30 Polyamide 12, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Especially suitable at dynamic stress situations.Electrically conductive, suitable for continuous discharging of statically generated electricity.Low waterabsorbtion, for dimensional stable precision parts.Bearings, sleeves, sliding elements, chair rollers, handles.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 165 MPa | 23900 psi | |
| Elongation at Yield | 3.7 % | 3.7 % | |
| 5.0 % | 5.0 % | flexural | |
| Modulus of Elasticity | 16.0 GPa | 2320 ksi | |
| Flexural Strength | 240 MPa | 34800 psi | |
| Flexural Modulus | 14.0 GPa | 2030 ksi | |
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | flatwise; ISO 179 1fU |
| 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179 1eA |
| 1.80 J/cm² @Temperature -30.0 °C |
8.57 ft-lb/in² @Temperature -22.0 °F |
ISO 179 eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 25.0 µm/m-°C | 13.9 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.500 W/m-K | 3.47 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |
| 140 °C | 284 °F | short term | |
| Vicat Softening Point | 170 °C | 338 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 100 ohm | <= 100 ohm | |
| Insulation Resistance | <= 100 ohm | <= 100 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 °C | 482 °F | mass temp |
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | |
| Zone 1 | 230 - 250 °C | 446 - 482 °F | |
| Zone 2 | 240 - 260 °C | 464 - 500 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 36000 sec |
167 °F @Time 6.00 - 10.0 hour |
Dehumidifying dryer |
| 105 °C @Time <=14400 sec |
221 °F @Time <=4.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Multibase TPSiV™ 3011-70A Thermoplastic Silicone Vulcanizate
- Pacific Sintered Materials FN-253-T(HT) 4600 Powdered Metal
- LG Chemical SEETEC H1501 Polypropylene Homopolymer
- SABIC Innovative Plastics LNP THERMOCOMP PX85100 PA 6
- SABIC Innovative Plastics LNP Thermocomp PZ006 PA 6 (Asia Pacific)
- Chevron Phillips Marlex® 9006 HDPE Injection Molding Resin
- Arlon Red Silicone Press Pad with Fiberglass Substrate (55393R045)
- Chem Polymer Durlex 700 PBT, General Purpose
- 3M Controltac™ 3500C Changeable Graphic Film with Comply™ Adhesive
- Sinotek Materials Graphite Sealing Strip Fireproofing Sealing Products
Copyright © lookpolymers.com All Rights Reserved