Gharda Chemicals GATONE™ 5300 PEEK, High Viscosity Grade  (discontinued **)

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Unreinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Gharda Chemicals GATONE™ 5300 PEEK, High Viscosity Grade  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High viscosity grade for extrusion and injection moldingCHARACTERISTICS: Outstanding chemical resistance.Outstanding wear resistance.Outstanding resistance to hydrolysis.Excellent mechanical properties.Outstanding thermal properties.Very good dielectric strength, volume resistivity, tracking resistance.Very good radiation resistance.Information provided by Gharda.Solvay Advanced Polymers completed its acquisition of this product line in May 2006.
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
ISO 118
Moisture Absorption at Equilibrium 0.50 %
0.50 %
ISO 62
Melt Flow 3.96 - 13.2 g/10 min

@Load 2.16 kg,
Temperature 400 °C
3.96 - 13.2 g/10 min

@Load 4.76 lb,
Temperature 752 °F
ASTM D1183
Mechanical Properties Metric English Comments
Tensile Strength at Break 95.0 MPa
13800 psi
ISO 527
Elongation at Break 45 %
45 %
ISO 527
Tensile Modulus 3.80 GPa
551 ksi
ISO 527
Flexural Strength 150 MPa
21800 psi
ISO 178
Flexural Modulus 4.00 GPa
580 ksi
ISO 178
Izod Impact, Notched 0.600 J/cm
1.12 ft-lb/in
ISO 179
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 260 °C
500 °F
(Expected) Continuous use, UL
Deflection Temperature at 1.8 MPa (264 psi) 150 °C
302 °F
ISO 75
Glass Transition Temp, Tg 148 °C
298 °F
DSC
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
IEC 93
Surface Resistance >= 1.00e+14 ohm
>= 1.00e+14 ohm
IEC 93
Dielectric Strength 19.0 kV/mm
483 kV/in
IEC 243/1