Lehmann & Voss LUVOCOM® 50-8479/BL-1 Polycarbonate, unreinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 50-8479/BL-1 Polycarbonate, unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Isotropic shrinkage characteristics.Reduced moment of inertia compared with metal parts.High dimensionally stable precision parts.Handles, levers, rollers, body parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ISO 1183 |
| Water Absorption | <= 0.20 % | <= 0.20 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | |
| Melt Flow | 24.48 g/10 min @Load 1.20 kg, Temperature 300 °C |
24.48 g/10 min @Load 2.65 lb, Temperature 572 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 55.0 MPa | 7980 psi | |
| Elongation at Yield | 5.0 % | 5.0 % | |
| 6.5 % | 6.5 % | flexural | |
| Modulus of Elasticity | 2.50 GPa | 363 ksi | |
| Flexural Strength | 80.0 MPa | 11600 psi | |
| Flexural Modulus | 2.00 GPa | 290 ksi | |
| Charpy Impact Unnotched | 11.0 J/cm² | 52.3 ft-lb/in² | flatwise; ISO 179 1fU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| 150 °C | 302 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 295 °C | 563 °F | mass temp |
| Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | |
| Zone 1 | 280 - 300 °C | 536 - 572 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 300 - 320 °C | 572 - 608 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | blue |
Users viewing this material also viewed the following:
- Polymer Resources PC-FR2A-D-[color]-3 Polycarbonate, Flame Retardant, Medium Flow, UV-stabilized
- Pau Tai Tribasic lead sulphate, Monomer Stabilizer
- Ineos A60-70-162 HDPE
- Samsung Cheil Industries Starex® ES-0173 ABS, Extrusion Grade
- Chase Plastics CP Pryme® A110 ABS, 10% Glass Fiber Reinforced
- Polyram PlusTek PA112NT Nylon 6.6, PTFE Filled
- ELASTO UK Dryflex® 8009-101 Flame Retardant TPE for Injection Molding, Black
- Dura-Bar 65-45-12 HRDS Continuously Cast Ductile Iron Bar Stock ASTM A536
- Carpenter BioDur™ 316LS Stainless Medical Implant Alloy, 70% Cold Worked
Copyright © lookpolymers.com All Rights Reserved