Ineos ABS Centrex® 485 ASA+AES Blend  (discontinued **)

Category	Polymer , Thermoplastic , AES Polymer , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Ineos ABS Centrex® 485 ASA+AES Blend  (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Key Features:UnfilledLight stabilized or stable to lightU.V. stabilized or stable to weatherSuitable processing methods:Profile extrusionSheet extrusionThermoformingInformation provided by Bayer Polymers.LANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majority shareholding under a JV with Lanxess in 2007. Subsequently Ineos acquired 100% of Ineos ABS.

Physical Properties	Metric	English	Comments
Density	1.05 g/cc	0.0379 lb/in³
Melt Flow	6.0 g/10 min <br>@Load 10.0 kg,<br> Temperature 220 °C	6.0 g/10 min <br>@Load 22.0 lb,<br> Temperature 428 °F	cm³/10 min.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	20.7 MPa	3000 psi
Elongation at Break	50 %	50 %	Nominal
Elongation at Yield	2.5 %	2.5 %
Tensile Modulus	1.45 GPa	210 ksi
Charpy Impact, Notched	1.07 J/cm²	5.09 ft-lb/in²
	0.240 J/cm² <br>@Temperature -30.0 °C	1.14 ft-lb/in² <br>@Temperature -22.0 °F

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	94.0 µm/m-°C <br>@Temperature 20.0 °C	52.2 µin/in-°F <br>@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	87.0 °C	189 °F
Deflection Temperature at 1.8 MPa (264 psi)	79.0 °C	174 °F
Vicat Softening Point	93.0 °C	199 °F	50°C/h 50N

Processing Properties	Metric	English	Comments
Melt Temperature	250 °C	482 °F	Injection Molding
Mold Temperature	60.0 °C	140 °F	Injection Molding
Injection Velocity	200 mm/sec	7.87 in/sec
Injection Pressure	60.0 MPa	8700 psi

Users viewing this material also viewed the following:

Ineos ABS Centrex® 485 ASA+AES Blend &nbsp;(discontinued **)

Ineos ABS Centrex® 485 ASA+AES Blend (discontinued **)