Cossa Polimeri ESTABLEND 8500 Polycarbonate ABS Blend
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTABLEND |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTABLEND 8500 Polycarbonate ABS Blend.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycarbonate and Acrylonitrile Butadiene Styrene blendHigh thermal resistance, high impact resistanceInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D 955 |
| Melt Flow | 13 g/10 min @Load 5.00 kg, Temperature 260 °C |
13 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ASTM D 638 |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | ASTM D 638 |
| Elongation at Break | 50 % | 50 % | ASTM D 638 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ASTM D 790 |
| Izod Impact, Notched | 4.50 J/cm @Temperature 0.000 °C |
8.43 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 |
| 5.00 J/cm @Temperature 23.0 °C |
9.37 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 132 °C @Load 5.00 kg |
270 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| 142 °C @Load 0.999 kg |
288 °F @Load 2.20 lb |
50°C/hr; ASTM D 1525 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Glow Wire Test | 750 °C | 1380 °F | I.E.C. 695-2-1 |
Users viewing this material also viewed the following:
- Eastman E6838-889P Polyethylene (discontinued **)
- Ineos ABS Lustran® M305
- Lucent Polymers CPP-0107 Polypropylene Homopolymer
- Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Conditioned)
- Shuman 502C Black Polypropylene Copolymer
- Shuman 780 Grey ABS
- Solvay MACKINE® 401 Surfactant
- Plenco 4311 Phenolic, Granular, Compression Molded
- Arlon 18609R023 0.023" (0.584 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- SABIC Innovative Plastics LNP Verton OV00A PPS
Copyright © lookpolymers.com All Rights Reserved