Lehmann & Voss LUVOCOM® 50-7446 Polycarbonate, with carbon fiber, PTFE, lubricant modified
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Carbon Fiber Reinforced |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 50-7446 Polycarbonate, with carbon fiber, PTFE, lubricant modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansion.Electrically conductive, suitable for continuous discharging of statically generated electricity.Improved friction and wear behaviour. Emergency running property.High dimensionally stable precision parts, even at elevated temperatures and narrow tolerance range.Body and duty parts in office equipment, gear wheels, grippers.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ISO 1183 |
| Water Absorption | <= 0.20 % | <= 0.20 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 105 MPa | 15200 psi | |
| Elongation at Yield | 2.0 % | 2.0 % | |
| 2.7 % | 2.7 % | flexural | |
| Modulus of Elasticity | 10.0 GPa | 1450 ksi | |
| Flexural Strength | 160 MPa | 23200 psi | |
| Flexural Modulus | 8.50 GPa | 1230 ksi | |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | flatwise; ISO 179 1fU |
| 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179 1eA |
| 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 179 eA | |
| Coefficient of Friction, Dynamic | 0.16 | 0.16 | |
| Coefficient of Friction, Static | 0.15 | 0.15 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.450 W/m-K | 3.12 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| 150 °C | 302 °F | short term | |
| Vicat Softening Point | 160 °C | 320 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1000 ohm | <= 1000 ohm | |
| Insulation Resistance | <= 1000 ohm | <= 1000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 295 °C | 563 °F | mass temp |
| Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | |
| Zone 1 | 280 - 300 °C | 536 - 572 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 300 - 320 °C | 572 - 608 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Proto3000 Objet TangoPlus FullCure930 Rubber-like Prototyping Polymer
- Zircar Zirconia ZYFB-6 Zirconia Boards, Discs, and Cylinders Insulation
- NOVA Chemicals Sclair® 2710 HDPE Injection Molding Resin
- Kolon SPESIN® KP212G30V0NB G/F Reinforced & Flame Retardant PBT Compound Resin
- Solvay TECHNYL® C 52G3 MZ25 PA6, Conditioned
- Techmer ES HiFill® PP GF/M50 CC BK 50% Glass/Mineral Filled
- Struktol STRUKSILON 8002 Silicone Stabilizer for PU-Rigid Foam
- Fainplast Compounds HG 78 Flexible PVC, Sheathing for High Temperatures
- Diamond Polymers ASA TWP 502
Copyright © lookpolymers.com All Rights Reserved