- Lehmann & Voss LUVOCOM® 2607-7921 Blend based on polyaryl ether ketone, unreinforced
Lehmann & Voss LUVOCOM® 2607-7921 Blend based on polyaryl ether ketone, unreinforced
| Category | Polymer , Thermoplastic , Polyketone |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 2607-7921 Blend based on polyaryl ether ketone, unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistanceHigh chemical resistance parts.Inherent flame resistance.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ISO 1183 |
| Water Absorption | <= 0.50 % | <= 0.50 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0060 - 0.011 cm/cm | 0.0060 - 0.011 in/in | |
| Melt Flow | 10.24 g/10 min @Load 1.20 kg, Temperature 380 °C |
10.24 g/10 min @Load 2.65 lb, Temperature 716 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 90.0 MPa | 13100 psi | |
| Elongation at Yield | 5.0 % | 5.0 % | |
| 6.5 % | 6.5 % | flexural | |
| Modulus of Elasticity | 3.00 GPa | 435 ksi | |
| Flexural Strength | 130 MPa | 18900 psi | |
| Flexural Modulus | 2.50 GPa | 363 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 200 °C | 392 °F | |
| 230 °C | 446 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 370 - 380 °C | 698 - 716 °F | |
| Zone 3 | 380 - 390 °C | 716 - 734 °F | |
| Mold Temperature | 160 - 200 °C | 320 - 392 °F | |
| Drying Temperature | 120 °C @Time >=18000 sec |
248 °F @Time >=5.00 hour |
|
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable W1800L Polyvinyl Chloride, Flexible (PVC, Flexible)
- Parker Chomerics ParPHorm® L1938-45 Non-Conductive Form-in-Place Gasket
- Panipol Oy W Dispersions Inherently Conductive Polymer
- Victrex® PEEK 90HMF40 Polyetheretherketone (PEEK), 40% Carbon Fiber Reinforced
- Industrial Laminates/Norplex MC507U Glass Fabric
- Struktol STRUKSILON 8018 Silicone Stabilizer for PU-Microcellular Foam
- A. Schulman PP 828S-01 Polypropylene Medium Impact Molding Grade Polypropylene
- DuPont™ Elvax® 3155 Ethylene Vinyl Acetate
- 3M Scotch-Weld™ CA8 Instant Adhesive
- SABIC Innovative Plastics LNP THERMOCOMP PH0800A PA 6
Copyright © lookpolymers.com All Rights Reserved