Lehmann & Voss LUVOCOM® 19-7669 Polyamide 46, with glass fiber and PTFE
| Category | Polymer , Thermoplastic , Nylon , Nylon 46 , Nylon 46, Lubricated + Glass Fiber Reinforced |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 19-7669 Polyamide 46, with glass fiber and PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Highly dimensionally stable at elevated temperatures.Gear parts for automotive appliances, control disks, cams, sliding elements.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ISO 1183 |
| Water Absorption | 1.5 % | 1.5 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 165 MPa | 23900 psi | |
| Elongation at Yield | 2.5 % | 2.5 % | |
| 3.0 % | 3.0 % | flexural | |
| Modulus of Elasticity | 10.0 GPa | 1450 ksi | |
| Flexural Strength | 240 MPa | 34800 psi | |
| Flexural Modulus | 8.00 GPa | 1160 ksi | |
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | ISO 179 1eA |
| Coefficient of Friction, Dynamic | 0.31 | 0.31 | |
| Coefficient of Friction, Static | 0.23 | 0.23 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 150 °C | 302 °F | |
| 240 °C | 464 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | |
| Vicat Softening Point | 290 °C | 554 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+9 ohm | >= 1.00e+9 ohm | |
| Insulation Resistance | >= 1.00e+9 ohm | >= 1.00e+9 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 310 °C | 590 °F | mass temp |
| Nozzle Temperature | 280 - 330 °C | 536 - 626 °F | |
| Zone 1 | 285 - 315 °C | 545 - 599 °F | |
| Zone 2 | 305 - 315 °C | 581 - 599 °F | |
| Zone 3 | 305 - 315 °C | 581 - 599 °F | |
| Mold Temperature | 120 - 140 °C | 248 - 284 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 43200 sec |
176 °F @Time 2.00 - 12.0 hour |
Vacuum Dryer |
| 80.0 °C @Time 7200 - 28800 sec |
176 °F @Time 2.00 - 8.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (beige) |
Users viewing this material also viewed the following:
- Resinlab® CYNERGY CA6806 Adhesive
- Kuraray HYBRAR® HD3 Thermoplastic Rubber-HDPE Blend
- SGL Carbon Group EK 3105 Carbon Graphite
- Teknor Apex Telcar® TL-1081A Thermoplastic Elastomer
- A. Schulman POLYBATCH™ Bright White P80514PF Concentrate Based In Polypropylene
- Hippe UP GM 202 Woven Glass Mat Reinforced Polyester (unsaturated) Resin - Sheet
- E-Polymers TEKASTER® F101F Fast cycle time PBT
- AKG Polymers Vision PP PPC BL3006 Polypropylene Copolymer Compound
- Bostik 120 Wood Adhesive EVA Glue Stick
- Momentive Performance Materials Silopren™ LSR 3386/30 Liquid Silicone Rubber - Self-Lubricating / Low Compression Set
Copyright © lookpolymers.com All Rights Reserved