Lehmann & Voss LUVOCOM® 19-7277 Polyamide 46, with carbon fiber and PTFE
| Category | Polymer , Thermoplastic , Nylon , Nylon 46 |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 19-7277 Polyamide 46, with carbon fiber and PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Reduced moment of inertia compared with metal parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Gear parts for automotive appliances, control disks, cams, sliding elements.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 210 MPa | 30500 psi | |
| Elongation at Yield | 2.0 % | 2.0 % | |
| 2.5 % | 2.5 % | flexural | |
| Modulus of Elasticity | 16.0 GPa | 2320 ksi | |
| Flexural Strength | 290 MPa | 42100 psi | |
| Flexural Modulus | 14.0 GPa | 2030 ksi | |
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 150 °C | 302 °F | |
| 160 °C | 320 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 290 °C | >= 554 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 10000 ohm | <= 10000 ohm | |
| Insulation Resistance | <= 100000 ohm | <= 100000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 310 °C | 590 °F | mass temp |
| Nozzle Temperature | 280 - 330 °C | 536 - 626 °F | |
| Zone 1 | 285 - 315 °C | 545 - 599 °F | |
| Zone 2 | 305 - 315 °C | 581 - 599 °F | |
| Zone 3 | 305 - 315 °C | 581 - 599 °F | |
| Mold Temperature | 120 - 140 °C | 248 - 284 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 43200 sec |
176 °F @Time 2.00 - 12.0 hour |
Vacuum Dryer |
| 80.0 °C @Time 7200 - 28800 sec |
176 °F @Time 2.00 - 8.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Pinnacle Polymers 1704 Polypropylene Homopolymer, Stretched Tape Grade
- Parker Chomerics CHO-FLEX 4432 Conductive Ink
- PolyOne Therma-Tech™ NJC-7500 Nylon 12 (discontinued **)
- Kennametal Stellite Tristelle TS-3 Iron Alloy
- Schott GM27884 Dental Glass
- Solvay Specialty Polymers Solef® 6012 Polyvinylidene Fluoride (PVDF)
- Teknor Apex APEX® 80128-Y Polyvinyl Chloride, Flexible
- DuPont Teijin Films Melinex® RFL1 Polyester Film, 600 Gauge
- Overview of materials for Ethylene-Methyl Acrylate Copolymer, Film Grade
Copyright © lookpolymers.com All Rights Reserved