Lehmann & Voss LUVOCOM® 19-7221/OR Polyamide 46, with glass fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 46 , Nylon 46, Glass Fiber Reinforced |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 19-7221/OR Polyamide 46, with glass fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Highly dimensionally stable at elevated temperatures.Gear parts for automotive appliances, control disks, cams, sliding elements.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ISO 1183 |
| Water Absorption | 1.5 % | 1.5 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 152 MPa | 22000 psi | |
| Elongation at Yield | 2.1 % | 2.1 % | |
| 2.5 % | 2.5 % | flexural | |
| Modulus of Elasticity | 9.80 GPa | 1420 ksi | |
| Flexural Strength | 215 MPa | 31200 psi | |
| Flexural Modulus | 8.50 GPa | 1230 ksi | |
| Charpy Impact Unnotched | 3.60 J/cm² | 17.1 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 35.0 µm/m-°C | 19.4 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.350 W/m-K | 2.43 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 150 °C | 302 °F | |
| 250 °C | 482 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 310 °C | 590 °F | mass temp |
| Nozzle Temperature | 280 - 330 °C | 536 - 626 °F | |
| Zone 1 | 285 - 315 °C | 545 - 599 °F | |
| Zone 2 | 305 - 315 °C | 581 - 599 °F | |
| Zone 3 | 305 - 315 °C | 581 - 599 °F | |
| Mold Temperature | 120 - 140 °C | 248 - 284 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 43200 sec |
176 °F @Time 2.00 - 12.0 hour |
Vacuum Dryer |
| 80.0 °C @Time 7200 - 28800 sec |
176 °F @Time 2.00 - 8.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | orange |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1105-7766 PEEK, with carbon fiber, easy flowing
- Fine Organics FINALUX G4 Lubricant Additive
- SABIC Innovative Plastics NORYL GTX GTX944 PPE+PA (Asia Pacific)
- Total PPM R020 Polypropylene, Random Copolymer for Medical Grade
- Toyobo PELPRENE™ P80C Polyester TPE, High Flexibility, High Melting Point
- Hexcel® HexTow™ 1900/IM Chopped Fiber
- Eurotec® Tecolen® CP20 GR20 NL XC30 PPCP, 20% glass fiber reinforced, flame retardant - halogen (RoHS compliant), heat stabilized, natural
- C.O.I.M. LARIPUR® LPR6560 PTMG Polyether Polyurethane
- Fainplast Compounds Hax™ HF 045/11 Flame Retardant Polyolefin Cable Compound
Copyright © lookpolymers.com All Rights Reserved