Lehmann & Voss LUVOCOM® 1850-7581 PBT, with carbon fiber and PTFE
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1850-7581 PBT, with carbon fiber and PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Electrically conductive, suitable for continuous discharging of statically generated electricity.Parts for electric and electronic industry.Coil formers, duty parts in plugs and switches, even combined with metal inserts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | |
| Melt Flow | 16.72 g/10 min @Load 5.00 kg, Temperature 250 °C |
16.72 g/10 min @Load 11.0 lb, Temperature 482 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 140 MPa | 20300 psi | |
| Elongation at Yield | 1.3 % | 1.3 % | |
| 1.6 % | 1.6 % | flexural | |
| Modulus of Elasticity | 20.0 GPa | 2900 ksi | |
| Flexural Strength | 195 MPa | 28300 psi | |
| Flexural Modulus | 17.0 GPa | 2470 ksi | |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | edgewise; ISO 179 1eU |
| Coefficient of Friction, Dynamic | 0.14 | 0.14 | |
| Coefficient of Friction, Static | 0.10 | 0.10 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| 180 °C | 356 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | |
| Vicat Softening Point | 210 °C | 410 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | <= 100 ohm | <= 100 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 °C | 482 °F | mass temp |
| Nozzle Temperature | 250 - 265 °C | 482 - 509 °F | |
| Zone 1 | 240 - 260 °C | 464 - 500 °F | |
| Zone 2 | 260 - 280 °C | 500 - 536 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | |
| Drying Temperature | 80.0 °C @Time 21600 - 28800 sec |
176 °F @Time 6.00 - 8.00 hour |
Vacuum Dryer |
| 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Permabond ET505 Epoxy Resin
- Cookson Group Plaskon® S-7P Epoxy Encapsulant (discontinued **)
- LG Chemical LS100 PVC
- Techmer ES Elastoblend® PA6/6 IM L UV Nylon 66
- A. Schulman PAPERMATCH® H-3818 Specialty Masterbatch
- Daikin NEOFLON NC-1539 FEP Coating Powder, Gray
- Diamond Polymers NPP25-0616 Black Impact Modified Polypropylene
- Fainplast Compounds HGKA 78 Flexible PVC, Sheathing for High Temperatures Lead Free
- Arlon 51393R032 0.032" (0.813 mm) Cured Silicone Rubber with Fiberglass Substrate
- RheTech Products GC20P600-01UV 20% Glass Fiber Reinforced Polypropylene, Chemically Coupled, UV Stabilized, Black
Copyright © lookpolymers.com All Rights Reserved