- Lehmann & Voss LUVOCOM® 1850-7431 PBT, with carbon fiber and glass spheres
Lehmann & Voss LUVOCOM® 1850-7431 PBT, with carbon fiber and glass spheres
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1850-7431 PBT, with carbon fiber and glass spheres.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Low warpage.Low waterabsorbtion, for dimensional stable precision parts.Parts for electric and electronic industry.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.53 g/cc | 1.53 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0070 - 0.012 cm/cm | 0.0070 - 0.012 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 70.0 MPa | 10200 psi | |
| Elongation at Yield | 2.1 % | 2.1 % | |
| 2.6 % | 2.6 % | flexural | |
| Modulus of Elasticity | 9.00 GPa | 1310 ksi | |
| Flexural Strength | 105 MPa | 15200 psi | |
| Flexural Modulus | 7.00 GPa | 1020 ksi | |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 120 °C | 248 °F | |
| 180 °C | 356 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+8 ohm | >= 1.00e+8 ohm | |
| Insulation Resistance | >= 1.00e+8 ohm | >= 1.00e+8 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 °C | 482 °F | mass temp |
| Nozzle Temperature | 250 - 265 °C | 482 - 509 °F | |
| Zone 1 | 240 - 260 °C | 464 - 500 °F | |
| Zone 2 | 260 - 280 °C | 500 - 536 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | |
| Drying Temperature | 80.0 °C @Time 21600 - 28800 sec |
176 °F @Time 6.00 - 8.00 hour |
Vacuum Dryer |
| 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Pyrotek EZ-400 Refractory Coating
- DSM Arnitel® EB500 Polyether Ester Elastomer (European and Asian Grade) (discontinued **)
- LATI Latamid 66 H2PX-V0 PA 66, Heat Stabilized, Flame Retardant
- Zircar Zirconia ZR-CEM Zirconia Cement
- Dow Corning FOX® PMCP15 Flowable Oxide
- Fainplast Compounds CKL 70 Flexible PVC, Sheathing Lead Free
- DuPont Performance Polymers Hytrel® HTR8223 BK320 Polyester Elastomer TPC-ET (Unverified Data**)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 1.0 PHR Thanecure® ZM
- SABIC Innovative Plastics Lexan® HFD4413 PC (Europe-Africa-Middle East)
- Huntsman PE8010 Specialty Polyethylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved