Lehmann & Voss LUVOCOM® 1501/CF/30-1 Polysulfone, with carbon fiber
| Category | Polymer , Thermoplastic , Polysulfone (PSU) , Polysulfone, Chopped Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1501/CF/30-1 Polysulfone, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, office machinery, medical- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precision parts, high continuous use temperature.Electrically conductive, suitable for continuous discharging of statically generated electricity.Control disks, gear wheels, pump impellers, gear parts for automotive appliances, chip carrier.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 160 MPa | 23200 psi | |
| Elongation at Yield | 1.5 % | 1.5 % | |
| 1.9 % | 1.9 % | flexural | |
| Modulus of Elasticity | 20.0 GPa | 2900 ksi | |
| Flexural Strength | 230 MPa | 33400 psi | |
| Flexural Modulus | 17.0 GPa | 2470 ksi | |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 11.0 µm/m-°C | 6.11 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 150 °C | 302 °F | |
| 170 °C | 338 °F | short term | |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 100 ohm | <= 100 ohm | |
| Insulation Resistance | <= 1000 ohm | <= 1000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 350 °C | 662 °F | mass temp |
| Nozzle Temperature | 350 - 370 °C | 662 - 698 °F | |
| Zone 1 | 330 - 350 °C | 626 - 662 °F | |
| Zone 2 | 340 - 360 °C | 644 - 680 °F | |
| Zone 3 | 350 - 370 °C | 662 - 698 °F | |
| Mold Temperature | 100 - 150 °C | 212 - 302 °F | |
| Drying Temperature | 140 °C @Time 10800 - 14400 sec |
284 °F @Time 3.00 - 4.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene® N OZO 5033 NBR-PVC blend
- Johnson Matthey SW 850 Platinum w/ 15% Iridium Jewelry Alloy
- Sharadaa Ceramics VELECRETE RC 105 Rodding Castables
- SABIC Innovative Plastics LNP Thermocomp IFB33 PA 6/12
- ExxonMobil Mobil Clean 10W-40 High Mileage
- Tra-Con Tra-Bond 546S02 Low Viscosity UV Curable Adhesive
- A. Schulman POLYBATCH™ Green 30424 Concentrate Based In Polyethylene
- Du-Co Ceramics S-470 Aluminum Silicate
- BASF Ultramid® B3K PA6 (Conditioned)
- ITW Plexus Plexus™ MA340 Methacrylate Adhesive
Copyright © lookpolymers.com All Rights Reserved