LATI Latilub 66-20T G/40 PA66, 40% Glass Fiber Reinforced, PTFE Filled

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber/PTFE Filled
Manufacturer LATI
Trade Name Latilub
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 66-20T G/40 PA66, 40% Glass Fiber Reinforced, PTFE Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polyamide 66 (PA66). PTFE. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.65 g/cc
0.0596 lb/in³
Linear Mold Shrinkage, Flow 0.0035 - 0.0060 cm/cm
0.0035 - 0.0060 in/in
Linear Mold Shrinkage, Transverse 0.0075 - 0.0105 cm/cm
0.0075 - 0.0105 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 170 MPa
24700 psi
Elongation at Break 2.0 %
2.0 %
Tensile Modulus 13.0 GPa
1890 ksi
Charpy Impact Unnotched 5.00 J/cm²
23.8 ft-lb/in²
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
Coefficient of Friction, Dynamic 0.29
0.29
Coefficient of Friction, Static 0.35
0.35
K (wear) Factor 5.10 x 10-8 mm³/N-M
2.53 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 270 °C
518 °F
Deflection Temperature at 1.8 MPa (264 psi) 260 °C
500 °F
Vicat Softening Point 250 °C

@Load 5.00 kg
482 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 275 - 300 °C
527 - 572 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa
Copyright © lookpolymers.com All Rights Reserved