Lehmann & Voss LUVOCOM® 1-8521 Polyamide 66, with carbon fiber and glass fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1-8521 Polyamide 66, with carbon fiber and glass fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Reduced moment of inertia compared with metal parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.High dimensionally stable precision parts with low warpage and narrow tolerance range.Gear parts for automotive appliances, control disks, cams, sliding elements.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 200 MPa | 29000 psi | |
| Elongation at Yield | 3.0 % | 3.0 % | |
| 4.0 % | 4.0 % | flexural | |
| Modulus of Elasticity | 11.0 GPa | 1600 ksi | |
| Flexural Strength | 290 MPa | 42100 psi | |
| Flexural Modulus | 9.50 GPa | 1380 ksi | |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 110 °C | 230 °F | |
| 140 °C | 284 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 10000 ohm | <= 10000 ohm | |
| Insulation Resistance | <= 10000 ohm | <= 10000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 290 °C | 554 °F | mass temp |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | |
| Zone 1 | 290 - 310 °C | 554 - 590 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 57600 sec |
167 °F @Time 6.00 - 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 21600 sec |
221 °F @Time 4.00 - 6.00 hour |
Vacuum Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- MV Labs LI300 Li2CO3 Lithium carbonate
- PolyOne Maxxam™ PPC-20T Nat Polypropylene Copolymer (PP Copolymer)
- Michelman® Michem® Emulsion 65435 Nonionic ethylene acrylic acid emulsion
- Silberline Silvet® AD 2000 LT20316
- ExxonMobil LLDPE LL 3402.48 Cast Linear Low Density Polyethylene Resin
- ExxonMobil Nexxstar™ EVA-00111 Low Density Polyethylene Resin
- Bapolene® 3042U Polyethylene, Rotational Molding Grade
- Ascend Performance Materials Vydyne® R530H BK02 Nylon 66, 30% Glass Reinforced, Conditioned
- Ascend Performance Materials Vydyne® R633 Nylon 66 Copolymer, 33% Glass Filled, Dry as Molded