Polyram RamTal PM3007G6 Acetal, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 30% Glass Fiber Reinforced |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamTal PM3007G6 Acetal, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass-fiber reinforced polyacetal for injection molding applications.Information provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.61 g/cc | 0.0582 lb/in³ | DIN 53479 |
| Water Absorption | 0.20 % | 0.20 % | DIN 53495 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 99 | 99 | ASTM-D785 |
| Tensile Strength, Yield | 135 MPa | 19600 psi | ASTM-D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM-D638 |
| Flexural Strength | 200 MPa | 29000 psi | ASTM-D790 |
| Flexural Modulus | 7.00 GPa | 1020 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.850 J/cm @Temperature 23.0 °C |
1.59 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | DIN 53461 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | DIN 53482 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Extrusion 87564 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Hyosung Topilene C600 PP
- Lehmann & Voss LUVOCOM® GS-H/2 Polyamide 66, lubricant modified
- Lubrizol Advanced Materials PEARLCOAT® 163K Thermoplastic Polyurethane Elastomer
- Silberline A-6571FG
- A. Schulman SCHULAFLEX® SF 302 Ethylene-Based Butene Plastomer
- A. Schulman POLYPUR™ FPU 1377 Thermoplastic Polyurethane Compound
- AK Steel 17-4 PH® Precipitation Hardening Stainless Steel, Condition H 925
- ATI Wah Chang 425™ Titanium Alloy, Hot Rolled & Annealed Plate
- China Tungsten ZY33 Tungsten Carbide for Mining Purposes
Copyright © lookpolymers.com All Rights Reserved