Lehmann & Voss LUVOCOM® 1-7893/GY Polyamide 66, with carbon fiber, heat stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1-7893/GY Polyamide 66, with carbon fiber, heat stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Reduced moment of inertia compared with metal parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.High dimensionally stable precision parts with low warpage and narrow tolerance range.Gear parts for automotive appliances, control disks, cams, sliding elements.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 245 MPa | 35500 psi | |
| Elongation at Yield | 1.6 % | 1.6 % | |
| 2.1 % | 2.1 % | flexural | |
| Modulus of Elasticity | 25.0 GPa | 3630 ksi | |
| Flexural Strength | 360 MPa | 52200 psi | |
| Flexural Modulus | 22.0 GPa | 3190 ksi | |
| Charpy Impact Unnotched | 4.80 J/cm² | 22.8 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 1.20 W/m-K | 8.33 BTU-in/hr-ft²-°F | HOT-DISK; 60x60x3 mm |
| Maximum Service Temperature, Air | 120 °C | 248 °F | |
| 160 °C | 320 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | |
| Vicat Softening Point | 260 °C | 500 °F | DIN ISO 306 |
| Flammability, UL94 | HB | HB | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 ohm | 100 ohm | |
| Insulation Resistance | 1000 ohm | 1000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 290 °C | 554 °F | mass temp |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | |
| Zone 1 | 290 - 310 °C | 554 - 590 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 57600 sec |
167 °F @Time 6.00 - 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 21600 sec |
221 °F @Time 4.00 - 6.00 hour |
Vacuum Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | dust grey |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPO D-6403
- PolyOne Geon™ Vinyl Wire & Cable Y594B Polyvinyl Chloride, Flexible (PVC, Flexible)
- Parker Chomerics CHO-FAB CRS Shielding Tape
- SABIC Innovative Plastics Lexan® ML7667 PC Copolymer (Europe-Africa-Middle East)
- Dow Pellethane® 2102-90AR Polyurethane Elastomer, Polyester Polycaprolactone Based (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP JCL36 PES (Europe-Africa-Middle East)
- SABIC Innovative Plastics Xenoy® CL100 PBT+PC (Asia Pacific)
- Eurotec® Tecopet® PT70 GR30 NL100 PR PET, 30% glass fiber reinforced, high heat stabilized, natural, fast crystallization grade
- Ascend Performance Materials Vydyne® R533 NT Nylon 66, 33% Glass Reinforced, Conditioned
- Adell BR-33 Nylon 6, 15% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved