- Lehmann & Voss LUVOCOM® 1-0890 Polyamide 66, with carbon fiber, low-warpage, heat stabilized
Lehmann & Voss LUVOCOM® 1-0890 Polyamide 66, with carbon fiber, low-warpage, heat stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1-0890 Polyamide 66, with carbon fiber, low-warpage, heat stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Stiff parts, low coefficient of expansion, low viscose, anisotropic.Reduced moment of inertia compared with metal parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Gear parts for automotive appliances, control disks, cams, sliding elements.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 200 MPa | 29000 psi | |
| Elongation at Yield | 2.0 % | 2.0 % | |
| 2.5 % | 2.5 % | flexural | |
| Modulus of Elasticity | 22.0 GPa | 3190 ksi | |
| Flexural Strength | 290 MPa | 42100 psi | |
| Flexural Modulus | 19.0 GPa | 2760 ksi | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.0 µm/m-°C | 6.67 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 120 °C | 248 °F | |
| 160 °C | 320 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | |
| Vicat Softening Point | 255 °C | 491 °F | DIN ISO 306 |
| Flammability, UL94 | HB | HB | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 100 ohm | <= 100 ohm | |
| Insulation Resistance | <= 100 ohm | <= 100 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 290 °C | 554 °F | mass temp |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | |
| Zone 1 | 290 - 310 °C | 554 - 590 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 57600 sec |
167 °F @Time 6.00 - 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 21600 sec |
221 °F @Time 4.00 - 6.00 hour |
Vacuum Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Potters Industries A-Series Premium 5MM Soda-Lime Silica Technical Quality Solid Glass Spheres
- ND Industries NutGrade® 122 Removable Threadlocker
- Polykemi AB POLYfill PP EIP2012 F Polypropylene, Mineral Reinforced, Extrusion grade, Low CLTE
- SABIC Innovative Plastics Geloy XTWM200 ASA (Europe-Africa-Middle East)
- LATI LATISTAT 30/R-05 High Impact Strength Polystyrene Base Conductive Plastic (discontinued **)
- Kolon KOCETAL® VT301 Anti-Static Grade Acetal Resin
- LG Chemical LUMID HI5001AH PA6/PO, High Melt Strength, High Barrier property, CaCl2 Resistance
- Kaneka PHBH Rigid Bio-based Polymer
- CP-Polymer-Technik Wellamid® 6000 GS 50 HWCP 50% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry
- Dow Corning 2-1912 FLUID
Copyright © lookpolymers.com All Rights Reserved