Lavergne VYPET VNT 245 PET - PBT 45% Glass Reinforced Polyester
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET) |
| Manufacturer | Lavergne Performance Compounds |
| Trade Name | VYPET |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lavergne VYPET VNT 245 PET - PBT 45% Glass Reinforced Polyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Vypet VNT 245 is a 45% fiberglass reinforced modified PBT / PET polyester injection molding compound designed for electrical and automotive applications requiring low warp and improved surface finish.Features: High temperature performance; Excellent strength and stiffness; Excellent dimensional stabilityTypical Applications: Automotive parts; Electric motor housingsInformation provided by Bieglo Gmbh for Lavergne Performance Compounds
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 2.00 mm |
0.0050 in/in @Thickness 0.0787 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 2.00 mm |
0.0090 in/in @Thickness 0.0787 in |
ASTM D955 |
| Ash | 45 % | 45 % | ASTM D2854 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 160 MPa | 23200 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 240 MPa | 34800 psi | 1.3 mm/min; ASTM D790 |
| Flexural Modulus | 13.8 GPa | 2000 ksi | 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm @Temperature 23.0 °C |
1.50 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C | 414 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 270 - 275 °C | 518 - 527 °F | |
| Front Barrel Temperature | 275 - 280 °C | 527 - 536 °F | |
| Nozzle Temperature | 275 - 290 °C | 527 - 554 °F | |
| Melt Temperature | 275 - 290 °C | 527 - 554 °F | |
| Mold Temperature | 75.0 - 100 °C | 167 - 212 °F | |
| Injection Pressure | 55.0 - 85.0 MPa | 7980 - 12300 psi |
Users viewing this material also viewed the following:
- Overview of materials for High Density Polyethylene (HDPE), Film Grade
- LG Chemical LUPOS GP-2200H General Purpose ABS, 20% Glass Fiber Reinforced, High Heat Resistance
- SABIC Innovative Plastics Ultem 1010V PEI
- Samsung Cheil Industries Starex® TF-0930 MABS, Unreinforced Scratch Resistant
- Sax Polymers SAXLAC 420HI Acrylonitrile Butadiene Styrene
- Dow Corning FS 1265 Fluid, 300 CST
- Diamond Polymers ABS 3002MC
- DuPont Teijin Films Melinex® S Polyester Film, 75 Gauge
- Azoty Tarnow™ TARFLEN SM-G15 PTFE
Copyright © lookpolymers.com All Rights Reserved