SABIC Innovative Plastics LNP VERTON RV00CESS PA6.6 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON RV00CESS PA6.6 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP Verton* RV00CESS is a compound based on PA 66 resin containing Long Glass Fiber. Added features include: Easy Molding, Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.71 g/cc | 0.0618 lb/in³ | ISO 1183 |
| Water Absorption | 0.90 % @Time 86400 sec |
0.90 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 279 MPa | 40500 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 281 MPa | 40800 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.7 % | 1.7 % | 5 mm/min; ISO 527 |
| 3.0 % | 3.0 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Elongation at Yield | 1.7 % | 1.7 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 21.6 GPa | 3130 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 418 MPa | 60600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 19.0 GPa | 2760 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 52.0 kJ/m² | 24.7 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 95.0 kJ/m² | 45.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 7204 LC BLK
- Nylene® 451 Nylon 6, 50% RH
- Braskem BI 818 LDPE Injection Molding Polyethylene (discontinued **)
- Gouda Vuurvast CURON 110 C Dense Refractory Castable
- Gromax BFG30-AH00B2 Nylon 6 30% Glass Filled (Conditioned)
- Spartech PP5210 Calcium Carbonate Filled Homopolymer
- Stellar Canada CERAMITE® SFR Wear Resistant Castable
- Crucible Steel PM M2 Tool Steel
- Clariant Renol 6642 2% Moly Nylon 66, Extrusion Grade, 2% Molybdenum Disulfide Lubricated
- Carpenter BioDur™ 316LS Stainless Medical Implant Alloy, 48% Cold Worked
Copyright © lookpolymers.com All Rights Reserved